Abstract:The human population is growing and needs more energy for optimal life. Since fossil fuel consumption is no longer accepted, new green energy sources are sought after, found, and further developed. One such energy carrier is hydrogen, which is used as fuel in various low-temperature proton exchange membrane (PEMFCs) and anion exchange membrane fuel cells (AEMFCs). 1 Unfortunately, these technologies are expensive due to the application of electrochemically active platinum-based catalysts. Thus, to make fuel cell technology more affordable: cheaper, more active, and more stable, non-Pt catalysts are researched and developed. For example, Ag has shown comparable and competitive results to Pt-based catalysts in an alkaline environment when used in AEMFCs. 2 In addition, Ag is nearly 50 times cheaper than Pt. In this work, Ag nanoparticles were deposited, using two different reducing agents – NaBH 4 and hydrazine hydrate, onto two novel mesoporous engineered carbon support (ECS) materials with a well-defined and uniform mesoporous structure with pore sizes of 8 and 35 nm for ECS004601, and 7 and 25 nm for ECS004201 (Pajarito Powder, LLC). For comparison, conventional Vulcan carbon XC-72R was used as a support to see whether the ECS supports promote better dispersion of Ag particles. SEM micrographs confirm that the synthesized Ag particles covered the mesoporous carbon support homogeneously. According to the XRD analysis, the average size of Ag crystallites remained between 19 and 28 nm. According to the thermogravimetric analysis, electrochemical Ag stripping, and SEM-EDX analysis, the amount of Ag in the catalysts after synthesis remained close to the nominal 40 wt%. Figure 1a shows that half-wave potentials ( E 1/2 ) remained in the range from -0.29 V to -0.37 V vs SCE, where catalyst Ag/4201_HH had the most positive E 1/2 , and bulk Ag electrode had the most negative. The electron transfer number n was close to four for all the Ag-based catalysts. Catalysts Ag/4201_HH and Ag/4601_BH4 had the biggest mass activities and showed good stability during 1000 potential cycles, where E 1/2 shifted only by 30 mV for Ag/4601_BH4 and 36 mV for Ag/4201_HH. Thus, these materials were tested in H 2 /O 2 AEMFC where Aemion+ anion exchange membrane was employed and Figure 1b shows that the peak power density for Ag/4201_HH was 243 mW cm -2 and for Ag/4601_BH4 310 mW cm -2 . Therefore, these materials are promising cathode catalysts for the AEMFC application. 3 References A. Sarapuu, E. Kibena-Poldsepp, M. Borghei, K. Tammeveski, Electrocatalysis of oxygen reduction on heteroatom-doped nanocarbons and transition metal-nitrogen-carbon catalysts for alkaline membrane fuel cells, Journal of Materials Chemistry A 6(3) (2018) 776-804. H. Erikson, A. Sarapuu, K. Tammeveski, Oxygen Reduction Reaction on Silver Catalysts in Alkaline Media: a Minireview, Chemelectrochem 6(1) (2019) 73-86. J. M. Linge, H. Erikson, M. Mooste, H-M Piirsoo, T. Kaljuvee, A. Kikas, J Aruväli, V. Kisand, A. Tamm, A. M. Kannan, K Tammeveski, Ag nanoparticles on mesoporous carbon support as cathode catalyst for anion exchange membrane fuel cell, International Journal of Hydrogen Energy (2023). Figure 1

Ag nanoparticles on mesoporous carbon support as cathode catalyst for anion exchange membrane fuel cell

Mesoporous Carbon Supported Ag-Based Catalyst for Anion Exchange Membrane Fuel Cell

Carbon Supported Silver Nanowires with Enhanced Catalytic Activity and Stability Used As A Cathode in A Direct Borohydride Fuel Cell

High-Performance Hydroxide Exchange Membrane Fuel Cell Comprising an Atomic Layer-Deposited Silver Cathode

Comparison of Carbon Supports in Anion Exchange Membrane Fuel Cells

Stability of Carbon Supported Silver Electrocatalysts for Alkaline Oxygen Reduction and Evolution Reactions

Direct One‐pot Synthesis of Carbon Supported Ag‐Pt Alloy Nanoparticles as High Performance Electrocatalyst for Fuel Cell Application

AgNPs@Fe-N-C oxygen reduction catalysts for anion exchange membrane fuel cells

Mesoporous iron-nitrogen co-doped carbon material as cathode catalyst for the anion exchange membrane fuel cell

Tunable Synthesis of Hollow Metal-Nitrogen-Carbon Capsules for Efficient Oxygen Reduction Catalysis in Proton Exchange Membrane Fuel Cells.

Transition Metal and Nitrogen-Doped Mesoporous Carbons As Cathode Catalysts for Anion-Exchange Membrane Fuel Cells

Nanofiber-Based Oxygen Reduction Electrocatalysts with Improved Mass Transfer Kinetics in a Meso-Porous Structure and Enhanced Reaction Kinetics by Confined Fe and Fe3C Particles for Anion-Exchange Membrane Fuel Cells

A nitrogen and fluorine enriched Fe/Fe3C@C oxygen reduction reaction electrocatalyst for anion/proton exchange membrane fuel cells

Oxygen reduction reaction on Ag nanocatalysts prepared by the microemulsion method

Electrooxidation of Formaldehyde on Silver/Ordered Mesoporous Carbon Composite Electrode in Alkaline Solutions

An easy synthesis of carbon-supported silver–cobalt bimetallic nanoparticles to study the electrocatalytic performance in alkaline borohydride fuel cell

Ionomer Cross-Linking Immobilization of Catalyst Nanoparticles for High Performance Alkaline Membrane Fuel Cells

(Digital Presentation) Synthesis of Proton Exchange Membrane Fuel Cell Catalyst and Optimization of Membrane Electrode Assembly Preparation Parameters

Directly anchoring Ag single atoms on α-MnO2 nanorods as efficient oxygen reduction catalysts for Mg-air fuel cell

Hybrid high-performance oxygen reduction reaction Fe–N–C electrocatalyst for anion exchange membrane fuel cells

Polythiophene, Polypyrrole and Carbon Nanotube-Based Catalyst for Alkaline Membrane Fuel Cell Cathode