Temperature Dependency of Hydrogen Embrittlement in Thermally H-precharged STS 304 Austenitic Stainless Steel

Hanna Yang,Thanh Tuan Nguyen,Jaeyeong Park,Hyeong Min Heo,Junghoon Lee,Un Bong Baek,Young-Kook Lee

DOI: https://doi.org/10.1007/s12540-022-01232-6

IF: 3.451

2022-06-04

Metals and Materials International

Abstract:In the present study, the resistance to hydrogen embrittlement (HE) of STS 304 austenitic stainless steel was investigated at a wide range of temperature from 25 to − 253 °C. Tensile specimens were thermally precharged with H at 300 °C for 35 days under a H 2 gas pressure of 10 MPa. The resistance to HE was reduced with decreasing tensile temperature from 25 to − 50 °C, and then increased again with decreasing deformation temperature further. Finally, HE disappeared at temperatures below − 150 °C. This temperature dependency of HE in thermally H-precharged specimens was almost the same as that in the specimens deformed in a H 2 gaseous environment. The occurrence of HE at the temperature range of 25 to − 50 °C was attributed to both strain-induced martensitic transformation (SIMT) and H diffusion into stress-concentrated regions. The absence of HE at temperatures below − 150 °C was due to the sluggish H diffusion, despite of active SIMT. Graphical

materials science, multidisciplinary,metallurgy & metallurgical engineering