Preparation of polyacrylonitrile-based solution blow spinning fluorescent nanofibers from perylene-doped silica nanoparticles
Albandary Almahri,Kholood Alkhamis,Ahmad Fawzi Qarah,Nada M. Alatawi,Abrar Bayazeed,Rua B. Alnoman,Nashwa M. El-Metwaly,Albandary AlmahriKholood AlkhamisAhmad Fawzi QarahNada M. AlatawiAbrar BayazeedRua B. AlnomanNashwa M. El-Metwalya Department of Chemistry,College of Science and Humanities in Al-Kharj,Prince Sattam Bin Abdulaziz University,Al-Kharj,Saudi Arabiab Department of Biochemistry,Faculty of Science,University of Tabuk,Tabuk,Saudi Arabiac Department of Chemistry,College of Science,Taibah University,Madinah,Saudi Arabiad Department of Chemistry,Faculty of Applied Science,Umm Al-Qura University,Makkah,Saudi Arabiae Department of Chemistry,Faculty of Science,Mansoura University,Mansoura,EgyptAlbandary Almahri is Assistance professor of analytical chemistry in Department of Chemistry,College of Science and Humanities in Al-Kharj,Prince Sattam Bin Abdulaziz University,Al-Kharj 11942,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. olood Alkhamis is Associate professor of inorganic chemistry in Department of Biochemistry,Faculty of Science,University of Tabuk,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. kalkhamis@ut.edu.saAhmad Fawzi Qarah is Associate professor of organic chemistry in Department of Chemistry,College of Science,Taibah University,Madinah,P. O. Box 344,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. aqarah@taibahu.edu.saNada M. Alatawi is Assistance professor of inorganic chemistry in Department of Chemistry,College of Science,Taibah University,Madinah,P. O. Box 344,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. nm-alatawy@ut.edu.saAbrar Bayazeed is Associate professor of organic chemistry in Department of Chemistry,College of Science,Taibah University,Madinah,P. O. chemistry in Department of Chemistry,Faculty of Applied Science,Umm Al-Qura University,Makkah 24230,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. aabayazeed@uqu.edu.saRua B. Alnoman is Associate professor of organic chemistry in Department of Chemistry,College of Science,Taibah University,Madinah,P. O. Box 344,Saudi Arabia. She taught all courses which covered the practical and theoretical in specialisation. rnoman@taibahu.edu.saNashwa M. El-Metwaly is A professor of inorganic chemistry in Department of Chemistry,Faculty of Applied Science,Umm Al-Qura University,Makkah 24230,Saudi Arabia and Department of Chemistry,Faculty of Science,Mansoura University,El-Gomhoria Street 35516,Egypt. She taught all courses which covered the practical and theoretical in specialisation. Also,I have a supervision for many students for postgraduate degree of master in chemistry. N_elmetwaly00@yahoo.com; nmmohamed@uqu.edu.sa
DOI: https://doi.org/10.1080/25740881.2023.2260870
2023-09-21
Polymer-Plastics Technology and Materials
Abstract:Fluorescent agents have been used to improve the anticounterfeiting of marketable products. It has been vital to enhance the engineering processing of fluorescent agents and materials matrices to prepare a mechanically reliable nanocomposite material with anticounterfeiting properties. Herein, new fluorescent and mechanically reliable inorganic-organic hybrid nanofibrous were developed by solution blowing spinning of polyacrylonitrile (PAN) encapsulating perylene-doped silica nanoparticles (PSiN). Two different types of fluorescent nanofibers were prepared using PSiN as an active doping agent and polyacrylonitrile as a hosting material. Fluorescent nanofibers were provided by solution blowing spinning technology utilizing perylene pigments, including perylene potassium (PMIK) and mono-imide sodium (PMINa) salts, and perylene diimide (PDI). In order to create a transparent nanofibrous film, fluorescent perylene-doped silica nanoparticles must be efficiently dispersed in a polyacrylonitrile solution without aggregation. The prepared fluorescent silica nanoparticles (SiN) displayed diameters ranging between 45 and 65 nm. The provided solution blow spun fluorescent PAN nanofibers integrated with PMINa, PMIK or PDI, showed smooth surface with diameters ranging between 350 and 550 nm. The prepared fluorescent PSiN and PSiN@PAN nanofibers were examined by several techniques, including transmission electron microscopy (TEM), scanning electron microscopy (SEM), and infrared spectroscopy (FT-IR). The solution blow spun nanofibers demonstrated an absorbance band at 458 nm and a fluorescence peak at 647 nm. The prepared nanofibers displayed a reversible emission upon repeated illumination with UV light. The emission properties of the prepared PSiN@PAN nanofibers were studied. The cytotoxic properties of the nanofibrous films were also explored. The current strategy introduces fluorescent nanostructured fibers that pave the way for the preparation of optical textiles such as optical devices, anticounterfeiting applications, and flexible displays.
polymer science