Synthesis, structural and optical characterizations of ZrO2-bromothymol blue nanocomposite thin-film [ZrO2+BTB]C and its application: experimental and TDD-DFT computations

Roaa T. Mogharbel,Ahmed F. Al-Hossainy,Ali. Ibrahim,Mohamed Abd El-Aal,Mohamed Sh. Zoromba,Samia M. Ibrahim,Asmaa Yahia,Nasser Farhan

DOI: https://doi.org/10.1007/s10854-022-08869-4

2022-08-18

Abstract:A [ZrO 2 +BTB] C nanocomposite was synthesized and prepared as a thin film using the sol–gel spin coating method. Different characterization techniques for [ZrO 2 +BTB] C like FTIR, UV–Vis, and optical properties have been used. The resulted XRD and SEM data have been employed to study interface composites. The optimization was performed using DFT by DMol 3 and CASTEP program. The chemical structure was confirmed by spectroscopic and structural properties for [ZrO 2 +BTB] C . XRD results showed the same crystal structure. Combined between experimental and TDD-DFT data, the average crystallite size and composite interface are 12.36 nm and orthorhombic symmetry ( a = 7.38(5); b = 18.178(6); c = 26.10(3) Å and a = b = g = 90°) with space group (P6 1 ) for [ZrO 2 +BTB] C , respectively, while those computed by DFT are 2.897 eV and 2.492 eV for as-isolated crystals of [BTB] TF and [ZrO 2 +BTB] C , respectively. Both [BTB] TF and [ZrO 2 +BTB] C thin films have direct allowed transitions. In addition, the optoelectrical parameters have been calculated for [BTB] TF and [ZrO 2 +BTB] C films such as refractive index, extinction coefficient, dielectric constant, and optical conductivity. The simulated values obtained by CATSTEP for the optical parameters of [ZrO 2 +BTB] C are in good agreement with the experimental values. PL technique analyses indicated two emission peaks appeared at 357 nm, and 497 nm for [ZrO 2 +BTB] C , whereas three emission peaks appeared at 335 nm, 383 nm, and 477 nm for [BTB] TF . The [ZrO 2 +BTB] C presents a good candidate for optoelectronics and solar cell applications.