Studies on optical properties, thermal stability and electrical conductivity of copper alumina nanoparticles-reinforced Poly(pyrrole-co-indole) for optoelectronic devices

S. Sankar,M. T. Ramesan

DOI: https://doi.org/10.1007/s10854-022-08965-5

2022-08-30

Abstract:This work focused on the effect of copper alumina (Cu–Al 2 O 3 ) nanoparticles in poly(pyrrole-co-indole) (PPy -co- PIN) on optical properties, thermal stability, alternating current (AC) conductivity, direct current (DC) conductivity and dielectric properties at different temperatures. Consistent distribution of Cu–Al 2 O 3 nanoparticles within the copolymer was observed from field-emission scanning electron microscopy. The single absorption seen (range 270 nm) in the UV spectra was due to π–π * transitions in the copolymeric materials. The minimum optical bandgap energy was observed for 5 wt% nanocomposite. From thermogravimetric analysis graph, maximum thermal resistance was observed for 7 wt% nanocomposite. The AC conductivity and dielectric parameters were dependent on both temperature and nanofillers loading and the maximum properties were found for 5 wt% nanocomposite. The AC conductivity and dielectric constant of 5 wt% nanocomposites were increased by 4.5 and 3 times, respectively, in comparison to (PPy-co-PIN). The decrease in activation energy with an increase in the content of Cu–Al 2 O 3 nanofillers and inverse dependence of Nyquist plot with temperature suggested semiconducting nature. The DC conductivity of copolymer was enhanced with encapsulation of Cu–Al 2 O 3 nanoparticles and the change in conductivity was correlated with Scarisbrick, Bueche and McCullough models. The McCullough model was in compromise with experimental conductivity values as it considers interfacial interactions. The match in theoretical and experimental conductivity values was advocating the presence of an efficient conductive pathway. The excellent properties of (PPy- co -PIN)/Cu–Al 2 O 3 nanocomposites can be exploited in concocting opto-electronic devices.