Optical limiting and nonlinear optical properties of silver nanoparticles embedded glasses containing rare-earth ions at 532 nm under nanosecond regime

Jagannath, Gangareddy

DOI: https://doi.org/10.1007/s10854-022-08527-9

2022-06-15

Abstract:Efficacy of silver nanoparticles concentration and annealing durations on optical limiting and optical nonlinearities of borate based glasses bearing the composition (79.5– x )B 2 O 3 –15Na 2 O–5La 2 O 3 –0.5Sm 2 O 3 – x AgCl (mol%) was assessed by Z-scan approach under the pumping of visible light (532 nm) in nanosecond regime. The dual photon absorption parameter (α 2 ) was elevated from 0.576 × 10 −11 to 1.201 × 10 −11 m/W with AgCl content from 0 to 0.5 mol%. This α 2 further raised to 1.964 × 10 −11 m/W when the optimized glass host heat treated at 450° C for 25 h. Similarly, the index of nonlinear refraction (n 2 ) was enhanced from 1.642 × 10 −19 to 2.532 × 10 −19 m 2 /W as the AgCl content increased from 0 to 0.5 mol%. This n 2 value in turn monotonously increased to 2.963 × 10 −19 m 2 /W when optimized glass system annealed at 450° C for 25 h. The optical limiting threshold magnitude followed reverse trend compared to α 2 and n 2 . The enhancement in nonlinear optical features and optical limiting efficiencies were related to field stimulated by Ag 0 nanoparticles when excited with high energy radiation. However, the non-uniform local field generated when the glass nanocomposites heated for longer duration resulted the switching of nonlinear absorption. The nonlinear optical and optical limiting results infer the 0.5 mol% AgCl encompassing glass sample annelaed at 450 °C for 25 h is benificail for construction of power optical limiters to operate in the visible range.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied