Improved energy storage property of ferroelectric polymer-based sandwiched composites interlayered with graphene oxide @ SiO2 core–shell nanoplatelets

Fan Yang,Hang Zhao,Chuying Zhang,Na Zhang,Tongguang Zhu,Lei Yin,Jinbo Bai

DOI: https://doi.org/10.1007/s10853-022-07380-9

IF: 4.5

2022-06-26

Journal of Materials Science

Abstract:The dielectric capacitors with high energy storage capability are demand for power electronic devices to keep pace with the development of the modern electronic and electrical industry. Although polymer-based dielectric composites showing the superiorities of ease processing, self-healing and low cost have a great potential in various applications, their energy storage capability is still severely limited by the negative coupling effect between dielectric permittivity and breakdown strength. In this study, we present a two-dimensional graphene oxide@silica core–shell nanoplatelets (GO@SiO 2 ) constructed through the classical Stöber method. Moreover, a series of polyvinylidene fluoride (PVDF)/GO@SiO 2 /PVDF sandwich-structured composites were assembled layer-by-layer and obtained through combining the spray coating and solution casting procedures. The GO@SiO 2 nanoplatelets were closely aligned and orientated along the direction that perpendicular to the electric field, forming the non-traditional inorganic middle layer. The thickness of the middle layer is dependent on the GO@SiO 2 loading fraction, which directly influenced the overall dielectric and electrical performances of the sandwich-structured composites. An enhanced breakdown strength (~ 253 MV m −1 ) and discharged density (~ 5.19 J cm −3 ) can be obtained from the PVDF/GO@SiO 2 /PVDF composite filled with the GO@SiO 2 loading fraction as small as 1.37 wt%, which are 23.4% and 161% higher than those of neat PVDF (~ 1.99 J cm −3 at 205 MV m −1 ), respectively. The improved energy storage capability could be attributed to the synergetic contribution of highly insulating SiO 2 shell, the additional core–shell interfacial interaction, the orientation that perpendicular to electric field and the multilayered construction of composite. Thus, this research provides a promising approach for the design of advanced composites with an improved dielectric energy storage property.

materials science, multidisciplinary