Abstract:Shrinkage deformation of concrete has been one of the difficulties in the process of concrete performance research. Cracking of concrete caused by self-shrinkage and temperature-drop shrinkage has become a common problem in the concrete world, and cracking leads to a decrease in the durability of concrete and even a safety hazard. Mineral admixtures, such as fly ash and mineral powder, are widely used to improve the temperature drop shrinkage of mass concrete; fly ash can reduce the temperature rise of concrete while also reducing the self-shrinkage of concrete, there are different results on the effect of mineral powder on the self-shrinkage of concrete, but the admixture of fly ash will reduce the strength of concrete, and mineral admixtures have an inhibitory effect on the shrinkage compensation effect of MgO expander(MEA). The paper investigates the effect of mineral admixtures on the mechanical and deformation properties of C50 mass concrete with a MgO expander(MEA), aiming to determine the proportion of C50 mass concrete with good anti-cracking properties under working conditions. The experiments investigated the effect of fly ash admixture, mineral powder admixture and MgO expander admixture on the compressive strength and deformation of concrete under simulated working conditions of variable temperature and analyzed the effect of hydration of magnesite in MgO expander and pore structure of cement paste on deformation. The following main conclusions were obtained: 1. When the concrete compounded with mineral admixture was cured under variable temperature conditions, the compounded 30% fly ash and mineral powder decreased by 4.3%, 6.0% and 8.4% at 7d age, and the compounded 40% fly ash and mineral powder decreased by 3.4%, 2.8% and 2.3% at 7d age, respectively. The incorporation of MEA reduced the early compressive strength of concrete; when the total amount of compounding remained unchanged, the early compressive strength of concrete was gradually smaller as the proportion of compounding decreased. 2. The results of concrete deformation showed that when the temperature rose, the concrete expanded rapidly, and when the temperature dropped, the concrete also showed a certain shrinkage, and the deformation of concrete basically reached stability at 18d. 3. The compounding of 30% fly ash and mineral powder As the compounding ratio decreases, the deformation of concrete increases, and the 28d deformation of concrete with a compounding ratio of 2:1 is 280 × 10-6, while the final stable deformation of concrete with a compounding ratio of 2:1 in compounding 40% fly ash and mineral powder is the largest, with a maximum value of 230 × 10-6, respectively. Overall, the concrete with a total compounding of 30% and a compounding ratio of 2:1 has the best shrinkage resistance performance.

Effects of submicron-MgO and nano-MgO on the expansion and microscopic properties of high-performance concrete

Engineering Performance and Expansion Mechanism of MgO Expansion Agent in Ultra-High Performance Concrete (UHPC)

Expansion Mechanism and Properties of Magnesium Oxide Expansive Hydraulic Cement for Engineering Applications

Hydration Characteristics and Expansive Mechanism of MgO Expansive Agents

Rheological, Deformation Behaviors and Mechanical Changes of Mgo-Containing Concretes with Different Strength

Influence of MgO on the Hydration and Shrinkage Behavior of Low Heat Portland Cement-Based Materials via Pore Structural and Fractal Analysis

Study On Long-Term Volume Stability And Microstructure Of Concrete Containing Magnesia Expansion Agent

Mitigation on the autogenous shrinkage of ultra-high performance concrete via using MgO expansive agent

Effect of graphene oxide on microstructure and micromechanical property of ultra-high performance concrete

Effect of Mineral Admixtures on the Mechanical and Shrinkage Performance of MgO Concrete

Optimization of Autogenous Volume Deformation Process Curve of MgO Concrete

The Influence of the Hydration Procedure of MgO Expansive Agent on the Expansive Behavior of Shrinkage-Compensating Mortar

Synergetic effect of magnesium oxide expansion additive and biochar on the deformation and mechanical properties of concrete

Systematic investigation into mechanical strength, pore structure and microstructure of high performance concrete incorporating nano-hybrids

Mechanical and micro-structure characteristics of cement-treated expansive soil admixed with nano-MgO

Analysis of Expansion Effect of Magnesium Oxide(mgo) in Mass Concrete

Mechanisms underlying the strength enhancement of UHPC modified with nano-SiO2 and nano-CaCO3

Effect of Nano-SiO2 on the Mechanical Properties, Microstructure, and Hydration Process of Cementitious Materials Incorporating Hydrophobic Admixture

Influence of Lightly Burned MgO on the Mechanical Properties and Anticarbonization of Cement-Based Materials

Mitigating shrinkage in ultra-high performance concrete using MgO expansion agents with different activity levels

Effect of Different Expansive Agents on the Deformation Properties of Core Concrete in a Steel Tube with a Harsh Temperature History