Enhanced Energy Storage Properties of Bi(Mg0.5Zr0.5)O3 Modified Ba0.9Sr0.1TiO3 Ceramics

Zhichao Xia,Yongqi Pan,Yi Chen,Zunping Xu

DOI: https://doi.org/10.1002/crat.202200147

2022-11-19

Crystal Research and Technology

Abstract:Lead‐free (1–x)Ba0.9Sr0.1TiO3–xBi(Mg0.5Zr0.5)O3 ((1–x)BST–xBMZ, x = 0–0.15) ceramics are synthesized by citrate combustion method. The typical relaxor characteristics and slimmer hysteresis loops are realized with x increasing. The optimal energy density with high efficiency is obtained for 0.9BST–0.1BMZ sample. More importantly, the energy storage properties of 0.9BST–0.1BMZ ceramic show excellent frequency stability and temperature stability. Lead‐free (1–x)Ba0.9Sr0.1TiO3–xBi(Mg0.5Zr0.5)O3 ((1–x)BST–xBMZ, x = 0–0.15) ceramics are synthesized via citrate combustion process. The grain size is reduced and slimmer hysteresis loops are realized as addition of BMZ. (1–x)BST–xBMZ ceramics exhibit typical relaxor characteristics as x increases. The recoverable energy storage density (Wre = 2.1 J cm−3) and efficiency (η = 88%) are obtained for 0.9BST‐0.1BMZ sample. The energy storage properties of 0.9BST‐0.1BMZ ceramic show excellent frequency stability (Wre varies 4.5% and η varies 1.8% at 5–100 Hz). Moreover, as the temperature increases from 25 °C to 100 °C, the variation of Wre is 7.1% and η keeps unchanged (88%) at 100 kV cm−1.

crystallography