Abstract:In order to study the characteristics and laws of nanocrack generation and self-healing behavior of asphalt materials under tensile action, the molecular dynamics (MD) method was used to simulate the continuous "tensile failure—self-healing" process, and this study remedies the shortcomings of existing experimental and observational methods. It is found that the MD-reproduced formation process of asphalt binder nanocrack contains four stages: "tensile extension", "nanocrack generation", "crack adding, expanding and penetrating" and "cracking failure". The influence of tensile conditions on the tensile cracking simulation of an asphalt binder model was analyzed, and it was found that low temperature and high loading rate would increase the tensile strength of the asphalt binder model. In addition, the MD-reproduced healing process of asphalt binder nanocracks can be divided into four stages: "surface approach", "surface rearrangement", "surface wetting" and "diffusion", which is similar to the healing process of polymers. Finally, from the perspective of energy change, the change rule of dominant van der Waals energy in the self-healing process was studied. Based on the existing research, the influence of damage degree on the healing performance of asphalt binder and its mechanism were further analyzed. The research results further enrich the theoretical research on microlevel cracking and healing of asphalt materials, and have certain theoretical value for the further development of self-healing asphalt materials.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the characteristics and laws of the generation and self - healing behavior of nano - cracks in asphalt materials under tensile action. Specifically, the author hopes to simulate the continuous "tensile failure - self - healing" process by the molecular dynamics (MD) method to make up for the deficiencies of existing experimental and observational methods.
### Research Background and Problem Description
Asphalt material is a complex viscoelastic material, which is widely used in road construction. However, cracks will gradually appear in asphalt pavements during use. These cracks have a relatively small impact on the flatness of the pavement and driving comfort in the early stage, but they will expand in a humid environment and lead to problems such as water damage, seriously affecting the performance and service life of the pavement. Therefore, how to avoid or repair the cracks in asphalt pavements has always been a hot issue for researchers.
### Core Problems of the Paper
1. **Nano - crack Generation Mechanism**: Study the generation process of nano - cracks in asphalt materials under tensile action and its influencing factors.
2. **Self - healing Behavior Analysis**: Explore the self - healing behavior of asphalt materials, especially the self - healing process and mechanism of nano - cracks.
3. **Influence of Temperature and Loading Rate**: Analyze the influence of different temperatures and loading rates on the tensile fracture and self - healing properties of asphalt materials.
### Research Methods
To achieve the above goals, the author adopts the molecular dynamics (MD) method and conducts research through the following steps:
1. **Establishment of Asphalt Material Molecular Model**: Select a multi - component model, including four components: saturated, aromatic, resin, and asphaltene, to construct the molecular model of asphalt material.
2. **Tensile Simulation**: Apply a constant deformation to the stable asphalt molecular model to simulate its tensile behavior at different temperatures and loading rates.
3. **Self - healing Simulation**: Use the nano - crack model obtained from the tensile simulation to further analyze the self - healing process of asphalt materials.
### Main Findings
- The nano - crack generation process of asphalt materials can be divided into four stages: "tensile elongation", "nano - crack generation", "crack expansion and penetration", and "fracture failure".
- The self - healing process can also be divided into four stages: "surface approach", "surface rearrangement", "surface wetting", and "diffusion", similar to the self - healing process of polymer materials.
- Low temperature and high loading rate will increase the tensile strength of asphalt materials.
- In the self - healing process, the change law of the dominant van der Waals energy indicates that the self - healing ability is closely related to the degree of damage.
### Conclusion
This research, through molecular dynamics simulation, deeply explores the crack generation and self - healing mechanisms of asphalt materials on a microscopic scale, providing a theoretical basis for the development of asphalt materials with better self - healing properties.