Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Polycarbosilane as a modulator for reaction-bonded silicon carbide processing of GNPs/Si mixtures

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

SiC-based Ceramic Materials Incorporating GNPs Array:Preparation and Mechanical Characterization

Mechanical and Tribological Properties of SiC-GNPs Composites Prepared by Oscillatory Pressure Sintering

Effect of polycarbosilane content on microstructures and mechanical properties of short-carbon-fibre-reinforced SiC composites

Enhanced strength and toughness of silicon carbide ceramics by graphene platelet-derived laminated reinforcement

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Coating dense Silicon Carbide layer on artificial graphites to achieve synergistically enhanced thermal conductivity and electronic insulation of polymer composites

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

Catalytic and Enhanced Effects of Silicon Carbide Nanoparticles on Carbonization and Graphitization of Polyimide Films

Microstructure and Mechanical Properties of SiC-GNPS-SiCW Ceramics by Oscillatory Pressure Sintering

Effects of silicon addition on the microstructure and properties of B 4 C–SiC composite prepared with polycarbosilane-coated B 4 C powder

Fabrication of Silicon Carbide (sic) Coatings from Pyrolysis of Polycarbosilane/Aluminum

Controllable reduction of absorbance and two-step reaction for 3D-printed SiC ceramics with micron-level periodic structure

A novel oxidation resistant SiC/B 4 C/C nanocomposite derived from a carborane-containing conjugated polycarbosilane

Preparation and Properties of Reaction Bonded Silicon Carbide (Rb-Sic) Ceramics with High SiC Percentage by Two-Step Sintering Using Compound Carbon Sources

In-Situ Generation of Sic Coating by Polycarbosilane Pyrolysis

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles

Preparation of SiC Coated Graphite Composite Powders by Nitriding Combustion Synthesis

Evaluation of Poly(methylsilane‐carbosilane) Synthesized from Methyl‐dichlorosilane and Chloromethyldichloromethylsilane As a Precursor for SiC

Preferentially oriented SiC/graphene composites for enhanced mechanical and thermal properties