Abstract:1. Srx(Zr0.9Y0.05Yb0.05)O1.95+x‐NiCoCrAlY thermal barrier coatings (TBCs) [SZYY‐1, x = 1.0; SZYY‐2, x = 0.9; SZYY‐3, x = 0.8] were deposited by suspension plasma spraying (SPS) using the corresponding precursors suspension prepared by co‐precipitation. 2. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of 1121°C‐1 h high‐temperature thermal cycling, up to 345 times. 3. The effects of microstructure and phase composition on thermal cycling failure of the coating at high temperatures were studied in detail. A finite element model was also proposed to evaluate the thermal stress thermally grown oxide (TGO) morphology of a real coating at different thermal cycling stages. The thermal barrier coatings (TBCs) consisting of Srx(Zr0.9Y0.05Yb0.05)O1.95+x were prepared using the suspension plasma spraying (SPS) method. Precursor suspensions were prepared via co‐precipitation for this purpose. Detailed microstructural, phase composition, and phase content analyses were conducted on these coatings, designated as SZYY‐1 (x = 1.0), SZYY‐2 (x = 0.9), and SZYY‐3 (x = 0.8). Additionally, the coatings underwent a thermal cycling test at 1121°C for 1 h. To assess the morphology of thermally grown oxide (TGO) in a real coating, a finite element model was employed. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of thermal cycling, up to 345 times. The thermophysical high‐temperature properties of the coating can be effectively improved through suitable second‐phase content. Microstructural and finite element analyses revealed that stress, primarily caused by the continuous growth of the Co3O4, NiO and Spinel (CNS) layer within TGO, was the predominant factor leading to coating failure. At elevated temperatures, transverse cracks formed at the interface between the bond coating and ceramic top coating due to mismatched thermal expansion and sintering effects, ultimately leading to coating degradation. Therefore, reducing the generation rate of large stresses in the coating, especially shear stresses, can effectively prevent the generation and propagation of transverse cracks and increase the thermal cycling life of TBCs.

Effect of Solution Precursor on Microstructure and High-Temperature Properties of the Thermal Barrier Coating Made by Solution Precursor Plasma Spray (SPPS) Process

Solution Medium Suspension Plasma Spray (SMSPS): A Microstructure and High-Temperature Properties Analysis of YSZ Thermal Barrier Coating

Microstructure and Thermophysical Properties of SrZrO3 Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray

Deposition Characteristics of SrZrO3 Thermal Barrier Coating Prepared by Solution Precursor Plasma Spray Process

Microstructural Design and Properties of Supersonic Suspension Plasma Sprayed Thermal Barrier Coatings

Review of suspension and solution precursor plasma sprayed thermal barrier coatings

A comparative study on the performance of suspension plasma sprayed thermal barrier coatings with different bond coat systems

Low Thermal Conductivity Yttrium Aluminum Garnet Thermal Barrier Coatings Made by the Solution Precursor Plasma Spray: Part I—Processing and Properties

Thermal cycling behavior of Srx(Zr0.9Y0.05Yb0.05)O1.95+x thermal barrier coatings by suspension plasma spraying

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch

High Performance Nanostructured ZrO2 Based Thermal Barrier Coatings Deposited by High Efficiency Supersonic Plasma Spraying

Structure–property differences between supersonic and conventional atmospheric plasma sprayed zirconia thermal barrier coatings

Effect of Suspension Plasma-Sprayed YSZ Columnar Microstructure and Bond Coat Surface Preparation on Thermal Barrier Coating Properties

Deposition Characteristics, Sintering and Cmas Corrosion Resistance, and Mechanical Properties of Thermal Barrier Coatings by Atmospheric Plasma Spraying

Low Thermal Conductivity Yttrium Aluminum Garnet Thermal Barrier Coatings Made by the Solution Precursor Plasma Spray: Part II—Planar Pore Formation and CMAS Resistance

Control of the Pore Structure of Plasma-Sprayed Thermal Barrier Coatings Through the Addition of Unmelted Porous YSZ Particles

Highly Segmented Thermal Barrier Coatings Deposited by Suspension Plasma Spray: Effects of Spray Process on Microstructure

Multi-layered Thermal Barrier Coatings Fabricated by Plasma-Spraying and Dry-Ice Blasting: Microstructure Characterization and Prolonged Lifetime

Lifetime Extension of Atmospheric and Suspension Plasma-Sprayed Thermal Barrier Coatings in Burner Rig Tests by Pre-Oxidizing the CoNiCrAlY Bond Coats

Air Plasma Sprayed Thermal Barrier Coatings on Titanium Alloy Substrates

Achieving high anti-sintering performance of plasma-sprayed YSZ thermal barrier coatings through pore structure design