Impact of nanoconfinement on the physical state and conductivity mechanisms of a 2-picolinium ionic liquid crystal
Andreia F. M. Santos,M. Teresa Viciosa,Inês Matos,João C. Sotomayor,João L. Figueirinhas,Maria H. Godinho,Luis C. Branco,C.J. Dias,Madalena Dionísio
DOI: https://doi.org/10.1016/j.molliq.2024.124830
IF: 6
2024-05-04
Journal of Molecular Liquids
Abstract:Hybrid solid-like materials prepared from the incorporation of liquid-like ionic conductors into nanoporous matrices could represent an advantage for a variety of electronic applications. Aiming to obtain such materials, three composites of the polymorphic ionic liquid crystal (ILC) 1-hexadecyl-2-methylpyridinium bromide ([C 16 -2-Pic][Br]), loaded in the mesoporous inorganic silica SBA-15 (∼6.8 nm in pore diameter), were prepared at guest–host weight fractions of ∼ 40, 60 and 80% (w/w) and investigated by different techniques: ATR-FTIR, BET, TGA, XRD and DSC. Complete amorphisation was achieved for the 40 and 60% composites, while the 80% preparation was stabilised in the low- T morph of native C 16 , being in the liquid state at room temperature. Furthermore, through Dielectric Relaxation Spectroscopy, the ionic conductivity of the three hybrid materials was characterised, allowing to deconvolute this property in a pure ohmic contribution (conductivity I) and the overlapping of ac − dc transition with interfacial polarisation resulting from the coexistence of the ionic liquid and the quasi-insulating inorganic matrix (conductivity II). From –20 to 20 °C, the conductivity and the corresponding charge migration are faster in all composites relative to the neat ILC, as deduced from the inferior radii of Nyquist arcs. The 60% preparation stood out from the other materials, exhibiting direct conductivity unaffected by electrode polarisation over a larger T -range, leading to the assumption of a nearly continuous silica-mediated charge migration pathway, which is never reached for the 40% composite, while, in the 80% preparation, some C 16 deposits on the outer surface of the pores. Incorporation into the silica matrix proved to be a good strategy for the production of cost-efficient materials with long-term stabilisation of the ionic liquid in a single phase over a large range of temperatures, enabling the prediction of flow and conductive properties.
chemistry, physical,physics, atomic, molecular & chemical