Abstract:The influence of orientation on the creep rupture properties of a single crystal superalloy DD6 under multiaxial stress was carried out at 980 degrees C and 400 MPa. A circumferential V-type notched specimen had been designed to investigate the effect of multiaxial stress state on the creep behavior. It was found that the creep lifetimes of the [111] oriented notched specimen were slightly longer than that of the [011] orientation and 1.36 times longer than that of the [001] orientation. The computational results showed that the strain and damage distribution revealed fourfold symmetry, double symmetry and threefold symmetry for [001], [011] and [111] orientation respectively, which was confirmed by experimental observation. At high temperature the creep anisotropy in three different orientations exhibited mainly in primary and secondary creep stages. Through the study of notched specimens by SEM, the morphology evolution of gamma'-phase proved that the directional coarsening was strongly dependent on the local effective stress and the direction of the local max principal stress with respect to loading axis. Fracture morphology displayed uneven cleavage configuration with multi-level feature, and the cleavage planes parallels (001), (011) and (111) crystal plane for [001], [011] and [111] orientation, respectively. The cleavage plane, which is attributed to the cracks propagated along the interfaces of gamma/gamma'phases, displayed square-like, rhombus-like and hexagon-like feature for [001], [011] and [111] orientation, respectively. Due to the higher density in dislocations of {111} planes, it is more easily as the secondary crack when the crack reach the {111} planes, which is thought to be the main reason of forming different feature on primary cleavage plane. (C) 2016 Elsevier B.V. All rights reserved.

Anisotropic Tensile Properties in Ni-Based Single-Crystal Superalloy DD6 near [001] Orientation at 760°C

Tensile Behavior of Nickel-Base Single-Crystal Superalloy DD6

Intermediate Temperature Brittleness and Directional Coarsening Behavior of Nickel-Based Single-Crystal Superalloy DD6

Anisotropic Creep Damage and Fracture Mechanism of Nickel-Base Single Crystal Superalloy under Multiaxial Stress

Effects of Long-Term Aging on the Microstructures and Tensile Properties of Ni-Based Single Crystal Superalloy

Tension/compression Asymmetry of [001] Single-Crystal Nickel-Based Superalloy DD6 During Low Cycle Fatigue

Microstructure Characterization and Damage Coupled Constitutive Modeling of Nickel-Based Single-Crystal Alloy with Different Orientations

Atomic Simulation of the Effect of Orientation on Tensile/compressive Properties in Nickel-Based Single Crystal Superalloys

Tensile Properties of DD15 Single Crystal Superalloy at Different Temperature

Orientation and temperature dependence of yielding and deformation behavior of a nickel-base single crystal superalloy

Influences of the Γ′ Phase on the Mechanical Properties of a Nickel-Based Single Crystal Superalloy

Transient Thermal Fatigue Crack Propagation Behavior of a Nickel-Based Single-Crystal Superalloy

Dependence on Temperature of Tensile Properties of the Single-Crystal Superalloy DD11

Anisotropic Behavior of Tensile Properties in a Hot-Extruded Polycrystalline Nickel-Base Superalloy

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

The Tension/compression Asymmetry of a High Γ′ Volume Fraction Nickel-based Single-Crystal Superalloy

Lattice Rotation and Deformation Mechanisms under Tensile Loading in a Single-Crystal Superalloy with [001] Misorientation

Orientation Effects on the Tensile Properties of Single Crystal Nickel with Nanovoid: Atomistic Simulation

Fretting Fatigue Failure Behavior of Nickel-based Single Crystal Superalloy Dovetail Specimen in Contact with Powder Metallurgy Pads at High Temperature

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

Long-term Oxidation Behavior and Mechanism of DD6 Ni-based Single Crystal Superalloy at 1050 °C and 1100 °C in Air