Abstract:The microstructural features and mechanical properties of composites formed by spark plasma sintering (SPS) of Al + 20 vol.% Fe and Al + 20 vol.% Fe66Cr10Nb5B19 (glassy alloy) mixtures composed of micrometer-sized particles are presented. The interaction between the mixture components was studied by differential thermal analysis and through examining the microstructure of composites sintered at two different SPS pressures. When the pressure was increased from 40 MPa to 80 MPa, the thickness of the reaction products formed between the iron particles and aluminum increased due to a more intimate contact between the phases established at a higher pressure. When the metallic glass was substituted for iron, the pressure increase had an opposite effect. It was concluded that local overheating at the interface in the case of Al + 20 vol.% Fe66Cr10Nb5B19 composites governed the formation of the product layers at 40 MPa. The influence of the nature of reinforcement on the mechanical properties of the composites was analyzed, for which sintered materials with similar microstructural features were compared. In composites without the reaction products and composites with thin layers of the products, the hardness increased by 13–38% relative to the unreinforced sintered aluminum, the glassy alloy and iron inclusions producing similar outcomes. The effect of the nature of added particles on the hardness and compressive strength of composites was seen when the microstructure of the material was such that an efficient load transfer mechanism was operative. This was possible upon the formation of thick layers of reaction products. Upon compression, the strong glassy cores experienced fracture, the composite with the glassy component showing a higher strength than the composite containing core-shell structures with metallic iron cores.

Effect of the spark plasma sintering temperature on the microstructure and mechanical properties of a ceramic/metallic glass reinforced hybrid composite

Effect of Spark Plasma Sintering Temperature on the Microstructure and Thermophysical Properties of High-Silicon–Aluminum Composites

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

Effect of Spark Plasma Sintering Temperature on the Microstructure and Mechanical Properties of A Ti2alc/Tial Composite

Effect of Sintering Temperature on Microstructure and Mechanical Properties of Al2O3/TiAl In-Situ Composites

Mechanical properties and microstructure of spark plasma sintered Al2O3-SiCw-Si3N4 composite ceramic tool materials

Effect of Sintering Temperature on Microstructure and Mechanical Properties of Hot-Pressed Fe/FeAl2O4 Composite

Effect of Sintering Temperature on High-Entropy Alloy Particle Reinforced Aluminum Matrix Composites via Vacuum Hot-Pressing Sintering

Effect of sintering temperature on microstructure and mechanical properties of Al2O3/TiAl in situ composites

Microstructure and Mechanical Properties of the Spark Plasma Sintered Tac/Sic Composites: Effects of Sintering Temperatures

Effects of sintering temperature on mechanical properties of alumina fiber reinforced alumina matrix composites

Effect of Sintering Temperature on Al2O3/TiAl Composite from Ti-Al-TiO2-Eu2O3 System

The interface reaction of SiC/Al composites by spark plasma sintering

Microstructure and properties of ceramic particulate reinforced metallic glassy matrix composites fabricated by spark plasma sintering

Microstructure and Mechanical Properties of Composites Obtained by Spark Plasma Sintering of Al–Fe66Cr10Nb5B19 Metallic Glass Powder Mixtures

Effect of SiC on Microstructure, Phase Evolution, and Mechanical Properties of Spark-Plasma-Sintered High-Entropy Ceramic Composite

Chromium carbide, carbon nano tubes and carbon fibers reinforced magnesium matrix hybrid composites prepared by spark plasma sintering

Effect of spark plasma sintering temperature on the multi-scale microstructure evolution and mechanical properties of Ti 2 AlC/TiAl composites with network architecture

Effect of spark plasma sintering temperature on microstructure and mechanical properties of melt-spun TiAl alloys

Metallic Iron or a Fe-Based Glassy Alloy to Reinforce Aluminum: Reactions at the Interface during Spark Plasma Sintering and Mechanical Properties of the Composites

Microstructure and mechanical properties comparison between spark plasma sintered and microwave sintered Al-(SiC + B 4 C) composite