Corrosion resistance and corrosion mechanism of the superhydrophobic coating fabricated on aluminum alloy in the salt spray corrosion environment

Xi Zhang,Ao Gong,Yong Zheng,Xiangyu Xu,Xiaoyu Li,Yufan Li

DOI: https://doi.org/10.1002/pssa.202200301

2022-08-17

Abstract:A novel superhydrophobic coating was introduced to spread on the aluminum alloy via spraying the epoxy resin adhesive, F‐SiO2 nanoparticles, white fluorinated polyurethane coatings, and fluorosilicone varnishes. After a long time Neutral Salt Spray Accelerated Corrosion(NSSAC) test, the surface morphology, wettability of the superhydrophobic coating were individually characterized, and the corrosion mechanism, variation law of corrosion resistance of the superhydrophobic coating were studied respectively. With extending the time of NSSAC test, the protruding micro‐nano structure and cross‐linked network structure on the surface of the coating were dismantled increasingly, the contact angle of the coating was decreased gradually, and the Corrosion Current Density(CCD) of the coating was increased progressively. The protruding micro‐nano structure had been less damaged before the 5th d of NSSAC test, while the protruding micro‐nano structure almost completely disappeared after 30 d of the NSSAC test. The contact angle of the coating was 162.35° before the NSSAC test, which remained greater than 150° when the NSSAC test was carried out for the 7th d, but decreased to 119.63° after 70 d. The CCD of the coating increased from 2.00× 10‐9 A•cm‐2 to 4.62× 10‐7A•cm‐2, which was two orders of magnitude lower than that of the non‐corroded 2A12 aluminum alloy, after 70 d of the NSSAC test. This article is protected by copyright. All rights reserved.