Abstract:Lanthanum, yttrium, and cerium hydrides are the three most well-known superconducting binary hydrides (La-H, Y-H, and Ce-H systems), which have gained great attention in both theoretical and experimental studies. Recent studies have shown that ternary hydrides composed of lanthanum and yttrium can achieve high superconductivity around 253 K. In this study we employ the evolutionary-algorithm-based crystal structure prediction (CSP) method and first-principles calculations to investigate the stability and superconductivity of ternary hydrides composed of (Y, Ce) and (La, Ce) under high pressure. Our calculations show that there are multiple stable phases in Y-Ce-H and La-Ce-H systems, among which $P4/mmm$-YCeH$_{8}$, $P\bar{6}m2$-YCeH$_{18}$, $R\bar{3}m$-YCeH$_{20}$, $P4/mmm$-LaCeH$_{8}$, and $R\bar{3}m$-LaCeH$_{20}$ possessing H$_{18}$, H$_{29}$ and H$_{32}$ clathrate structures can maintain both the thermodynamic and lattice-dynamic stabilities. In addition, we also find that these phases also maintain a strong resistance to decomposition at high temperature. Electron-phonon coupling calculations show that only three of these five phases can exhibit high-temperature superconductivity. The superconducting transition temperatures ($T_\mathrm{c}$) of $R\bar{3}m$-YCeH$_{20}$, $R\bar{3}m$-LaCeH$_{20}$, and $P\bar{6}m2$-YCeH$_{18}$ are predicted using the Allen-Dynes-modified McMillan formula to be 122 K at 300 GPa, 116 K at 250 GPa, and 173 K at 150 GPa, respectively. Moreover, the pressure to stabilize $P\bar{6}m2$-YCeH$_{18}$ can be lowered to 150 GPa, suggesting an accessible condition for its high-pressure synthesis.

High-Temperature Structural Stability of Intercalated Cerium Superhydride into Graphene Sheets at Low Pressure

Criticality in electronic structure of two graphene layers containing praseodymium superhydride doped molecules

Predicted High-Temperature Superconductivity in Cerium Hydrides at High Pressures

High-Temperature Superconductivity in Cerium Superhydrides

High-Temperature Superconducting Phases in Cerium Superhydride with a T c up to 115 K below a Pressure of 1 Megabar

Synthesis and superconductivity in yttrium-cerium hydrides at high pressures

Computational Materials Discovery for Lanthanide Hydrides at high pressure: predicting High Temperature superconductivity

Potential high-$T_{c}$ superconductivity in YCeH$_{x}$ and LaCeH$_{x}$ under pressure

Superconductivity in the Ce–B–H system at high pressure

Pressure Phase Diagram and Quantum Criticality of Cept2in7 Single Crystals

High-temperature Superconductivity in Sulfur Hydride Evidenced by Alternating-Current Magnetic Susceptibility

Feasible route to high-temperature ambient-pressure hydride superconductivity

Synthesis of clathrate cerium superhydride CeH9 below 100 GPa with atomic hydrogen sublattice

Synthesis and Superconductivity in Yttrium-Cerium Hydrides at Moderate Pressures

Synthesis of clathrate cerium superhydride CeH9 at 80-100 GPa with atomic hydrogen sublattice

High-Te Superconductivity in Squeezed Cubic CSeH6 and C2TeH8 Ternary Polyhydrides

Synthesis of superconducting phase of La0.5Ce0.5H10at high pressures

Efficient route to achieve superconductivity improvement via substitutional La-Ce alloy superhydride at high pressure

Dynamical stability and superconductivity of (Ce,La)H9 under high pressure

Superconductivity in CH4 and BH4- Containing Compounds Derived from the High-Pressure Superhydrides

(La,Th)H 10 : Potential High- T c (242 K) Superconductors Stabilized Thermodynamically below 200 GPa