Structural and electrochemical properties of manganese oxide/rGO/PCL nanofiber for supercapacitor electrode material
Sagolsem Nonganbi Chanu,Pukhrambam Sushma Devi,Bibhu Prasad Swain,Swain, Bibhu Prasad
DOI: https://doi.org/10.1007/s10854-024-12411-z
2024-03-27
Journal of Materials Science Materials in Electronics
Abstract:In this work, manganese oxide (Mn 3 O 4 )/reduced graphene oxide (rGO)/polycaprolactone (PCL) electrospun nanofiber composite was synthesized for supercapacitor electrode applications. The SEM image showed nanofiber formation with an average diameter size ranging from 100 to 200 nm. The interlayer spacing (d) of rGO was 0.38 nm due to the oxygen functional group between the layers. The diffraction peak appeared at 19.4°, 31.4°, 32.5°, 36.1°, 44.5°, and 60.1° corresponding to (101), (112), (103), (211), (220), and (224) diffraction planes of Mn 3 O 4 /rGO/PCL nanofiber. The defect parameter (I D /I G ) varied from 1.05 to 1.17 for rGO, PCL/rGO and Mn 3 O 4 /rGO/PCL nanocomposites, respectively. The estimated particle size ( R g ) interdiffusion correlation length and surface fractal ( D s ) from small angle X-ray Scattering (SAXS) of electrospun Mn 3 O 4 /rGO/PCL nanofiber is estimated at 8.5 nm, 2.3 nm, and 1.17, respectively. The maximum specific capacitance ( C sp ) energy density and power density of Mn 3 O 4 /rGO/PCL nanofiber are 690 F/g, 17.46 Wh kg −1 , and 99.85 W kg −1 , respectively, at a current density of 1 A g −1 . In the analysis of corrosion, the I corr and E corr values for 1-M H 2 SO 4 and 1-M KCl electrolytes are determined to be 5.781 A and 1.76 A as well as 0.3 and 0.4 V, respectively.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied