Abstract:Multiphase CrMnFeCoNi high-entropy alloys (HEAs) were prepared by a powder metallurgy process combining mechanical alloying (MA) and vacuum hot-pressing sintering (HPS). The single-phase face-centered cubic (FCC) HEA powder prepared by MA was sintered into a bulk HEA specimen containing FCC phase matrix along with precipitated M23C6 phase and nanoscale σ phase particles. When the sintering temperature was 1223 K, the ultimate strength reaches 1300 ± 11.6 MPa, and the elongation exceeds 4% ± 0.6%. Microstructural characterization reveals that the formation of nanoscale particles and deformation twins play critical roles in improving the strain hardening (SH) ability. Prolonging the MA time promoted the formation of the precipitated phase and enhanced the SH ability by increasing the number of precipitated particles. The SH capacity increases significantly with increasing sintering temperature, which is attributed to a significant enhancement in the twinning capacity due to grain growth and the reduced number of σ phase particles. Through systematic studies, the planar glide of dislocations was found to be the main mode of deformation, while deformation twinning appeared as an auxiliary deformation mode when the twinning stress was reached. Although the formation of precipitates leads to grain boundary and precipitation strengthening effects, crack initiation is more prominent owing to increased grain boundary brittleness around the precipitated M23C6 phase. The prominence of crack initiation is a contradiction that must be reconciled with regard to precipitation strengthening. This work serves as a useful reference for the preparation of high-strength HEA parts by powder metallurgy.

Revealing strengthening contribution of grain refinement and phase precipitation in CrMnFeCoNi high-entropy alloy prepared from different powders

Strengthening and deformation mechanism of high-strength CrMnFeCoNi high entropy alloy prepared by powder metallurgy

Hot cracking, crystal orientation and compressive strength of an equimolar CoCrFeMnNi high-entropy alloy printed by selective laser melting

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Microstructural Evolution and Elevated-Temperature Strengthening Mechanism of Co-free FeCrMnNiV0.2Alx High-Entropy Alloys During Annealing

Unveiling the Precipitation Behavior and Mechanical Properties in G-phase Strengthened CrFe2Ni2Ti0.2Six Multi-Principal Element Alloys

Microstructural Evolution and Strengthening Mechanisms in CrxMnFeNi High-Entropy Alloy

Influence of in-situ and ex-situ precipitations on microstructure and mechanical properties of additive manufacturing CoCrFeMnNi high-entropy alloys

Microstructure and mechanical properties of CoCrFeNiTa high entropy alloy prepared by mechanical alloying and spark plasma sintering

Synthesis and Phase Evolution of a Nanocrystalline FexCrNiAl (x = 1.0, 0.5, 0.25) High-Entropy Alloys by Mechanical Alloying

Microstructure and mechanical properties of Al-Fe-Co-Cr-Ni high entropy alloy fabricated via powder extrusion

Carbide Precipitation Strengthening in Fine-Grained Carbon-Doped FeCoCrNiMn High Entropy Alloy

Strengthening of a CrMnFeCoNi High-Entropy Alloy by Carbide Precipitation

Multiscale-phase-driven strength-ductility synergy in Fe3Cr2CoNiAlx high entropy alloys

Unveiling the Precipitation Behavior and Mechanical Properties of Co-free Ni47-xFe30Cr12Mn8AlxTi3 High-Entropy Alloys

Grain growth and strengthening mechanisms of ultrafine-grained CoCrFeNiMn high entropy alloy matrix nanocomposites fabricated by powder metallurgy

Improving Mechanical Properties of Co-Cr-Fe-Ni High Entropy Alloy via C and Mo Microalloying

Microstructure evolution and mechanical behavior of a CoCrFeNiMn0.75Cu0.25 high-entropy alloy by thermo-mechanical treatment

Microstructure and mechanical properties of CrMnFeCoNi high entropy alloy/Al composite with different reinforcement content

Microstructures and properties of Fe1.25CoNi1.25CrxAl0.25 high-entropy alloys after cold-rolling and annealing

Mechanical properties and fracture mechanism of as-cast MnFeCoCuNi high-entropy alloys