Abstract:In this article, we report a novel, nanoprecipitation-based method for preparing silica nanoparticles with thiol and amine cofunctionalization. (3-Mercaptopropyl)trimethoxysilane (MPTMS) and 3-aminopropyltrimethoxysilane (APTMS) were used as the organosilane precursors, which were subjected to acid-catalyzed polycondensation in an organic phase containing a water-miscible solvent (e.g., dimethyl sulfoxide). A pale colloidal solution could be immediately formed when the preincubated organic phase was directly injected into water. The initial composition ratio between MPTMS and APTMS is an important factor governing the formation of nanoparticles. Specifically, large, unstable micrometer-sized particles were formed for preparation using MPTMS as the sole silane source. In contrast, when APTMS was used alone, no particles could be formed. By reducing the fraction of APTMS (or increasing that of MPTMS) in the initial mixture of organosilanes, the formation of nanometer-sized particles occurred at a critical fraction of APTMS (i.e., 25%). Remarkably, a tiny fraction (e.g., 1%) of APTMS was sufficient to produce stable nanoparticles with a hydrodynamic diameter of about 200 nm. Other factors that would also affect particle formation were determined. Moreover, an interesting temperature effect on particle formation was observed. The TEM micrographs show spherical nanospheres with mean sizes of 130-150 nm in diameter. The solid-state (29)Si NMR spectra demonstrate that the hybrid silica materials contain fully and partially condensed silicon structures. The bifunctionalized silica nanoparticles have positive zeta potentials whose magnitudes are positively correlated with the amount of APTMS. The total thiol content, however, is negatively correlated with the amount of APTMS. The cationic nanoparticles can bind an antisense oligonucleotide in a composition-dependent manner.

Eco-Friendly Synthesis of Organo-Functionalized Mesoporous Silica for the Condensation Reaction

Functionalized silica materials synthesized via co-condensation and post-grafting methods

Facile One-Pot Synthesis of Amine-Functionalized Mesoporous Silica Nanospheres for Water-Medium Knoevenagel Reaction Under Microwave Irradiation

Non-hydrolytic sol-gel synthesis of amine-functionalized silica: Template- and catalyst-free preparation of mesoporous catalysts for CO2 valorization

Magnetic nanoparticle supported amine: An efficient and environmental benign catalyst for versatile Knoevenagel condensation under ultrasound irradiation

Preparation of amine functionalized silica by the one-step in spray drying system

Synthesis of sulfonic SBA-15 by co-condensation and soxhlet extraction: optimization by shortening the preparation time

Synthesis and characterization of mesoporous and amorphous silica modified with silica-organo-sulfogroups

ChemInform Abstract: Nano‐Fe3O4 Encapsulated‐Silica Particles Bearing 3‐aminopropyl Group As a Magnetically Separable Catalyst for Efficient Knoevenagel Condensation of Aromatic Aldehydes with Active Methylene Compounds.

Mesoporous silica nanoparticles in an efficient solvent-free transamidation of carboxamides with amines: an exhibition of a green recyclable nanocatalyst

Sustainable Sulfonic Acid Functionalized Tubular Shape Mesoporous Silica as a Heterogeneous Catalyst for Selective Unsymmetrical Friedel-Crafts Alkylation in One Pot

Fine-tuning the degree of organic functionalization of mesoporous silica nanosphere materials via an interfacially designed co-condensation method

Amino-grafted basic mesoporous silicas: a type of highly performant catalysts for the green synthesis of 2-amino-4 H -chromenes

Sustainable synthesis of ordered mesoporous materials without additional solvents

Functionalization of Sba-15 Mesoporous Silica with Thiol or Sulfonic Acid Groups under the Crystallization Conditions

Synthesis and Characterization of Functionalize HY Zeolite With Sulfunic Acid, A Micro-meso Structure as an Efficient Reusable Catalyst in Organic Transformations

Mesoporous silica materials with an extremely high content of organic sulfonic groups and their comparable activities with that of concentrated sulfuric acid in catalytic esterification.

Sulfamic acid pyromellitic diamide-functionalized MCM-41 as a multifunctional hybrid catalyst for melting-assisted solvent-free synthesis of bioactive 3,4-dihydropyrimidin-2-(1H)-ones

One-Pot Synthesis of Amine-Functionalized Nano-Silica via Sol-Gel Assisted by Reverse Micelle Microemulsion for Environmental Application

Amine-containing yolk-shell structured magnetic organosilica nanocomposite as a highly efficient catalyst for the Knoevenagel reaction

Versatile Synthesis of Thiol- and Amine-Bifunctionalized Silica Nanoparticles Based on the Ouzo Effect