Preparation of Porous Si2N2O/SiC Ceramics by Microwave Sintering
Yuxuan Duan,Li Guan,Zhiyu Min,Ruijie Fu,Jiaxin Li,Lei Fan,Hamidreza Abadikhah,Biao Zhao,Binbin Dong,Rui Zhang
DOI: https://doi.org/10.1002/adem.202401649
IF: 3.6
2024-10-05
Advanced Engineering Materials
Abstract:Porous Si2N2O/SiC ceramics is facilitated at 1200 °C for 10 min by microwave sintering. Rapid in‐situ production of Si2N2O fibers provided high mechanical properties of the samples. The porosity of the prepared sample is tailorable and the thermal insulation effect is excellent. Two steps strategy were taken to effectively produce porous Si2N2O/SiC ceramics: 1) direct foaming combined with sol‐gel curing at room temperature to form a green body, and 2) sintering assisted by in‐situ production of Si2N2O fibers under microwave sintering conditions. Non‐toxic silica sol was used to provide silicon source for in‐situ synthesis of Si2N2O, the silica sol could form a gel that stabilizes the bubbles, creating a porous structure. A thorough investigation was conducted into how different sintering temperatures affected the microstructure, flexural strength, and porosity of the porous Si2N2O/SiC composites. The main bonding phase in the porous composites was the Si2N2O with fiber morphology. The optimal microwave sintering temperature for fabricating porous Si2N2O/SiC ceramics, using a combination of sol‐gel and direct foaming techniques, has been determined to be 1200 °C. At this temperature, the porosity can be controlled between 73.32% and 83.16% by proportionally adjusting the ratio of the raw materials. Under the condition of high porosity, the thermal radiation is dominant and the thermal conductivity increases with the increase of temperature. With the decrease of porosity, the heat conduction is dominant, and the thermal conductivity decreases with the increase of temperature.
materials science, multidisciplinary