Effects of graphene oxide (GO) on resistance to chloride-ion penetration of concrete

Surong Luo,Xin Li,Weiyi Lin,Dehui Wang
DOI: https://doi.org/10.1680/jmacr.21.00090
IF: 2.46
2022-06-17
Magazine of Concrete Research
Abstract:The effects of graphene oxide (GO) on the microstructure and resistance to chloride ion penetration of matrix were investigated. The hydration heat, hydration products, pore structure and chloride ion penetration of matrix containing 0-0.05% GO were tested by isothermal calorimeter, thermogravimetric analysis (TGA), X-ray diffraction (XRD), mercury intrusion porosimetry (MIP) and the rapid chloride penetration test (RCPT) method. A proper dosage of GO promoted the hydration process of cement, increased the calcium hydroxide (CH) content, refined the size of CH, promoted the formation of high density C-S-H and improved the pore size distribution of cement matrix. Compared to the group without GO, the porosity of concrete containing 0.03% GO decreased by 8.56%, the most pore diameter decreased by 29.05%, and the pores larger than 50nm were reduced by 36.93%. In addition, the incorporation of GO improved the resistance to chloride penetration of concrete. The charge passed through the concrete decreased firstly and then increased with the increasing GO dosage. When the dosage of GO was 0.03%, the charge passed through the concrete was 27.71% lower than that of the control group. There was a significant correlation between the permeability of chloride ions and pore structure, especially the proportion of pores larger than 50nm (>50nm) of concrete.
construction & building technology,materials science, multidisciplinary
What problem does this paper attempt to address?