Modification of the Electronic Structure and Surface State of LaFeO3 for Improved Visible Light Photoelectrochemical Water Oxidation
Qi Peng,Yanwei Wen,Bin Shan,Rong Chen
DOI: https://doi.org/10.1149/ma2016-02/49/3658
2016-01-01
ECS Meeting Abstracts
Abstract:Photocatalytic hydrogen generation by solar energy is a promising approach to clean energy resource and has attracted great attention over the past decades. [1] Perovskites ABO3 structures provide the basic stable framework to both crystal and electronic structures modification, which have found extensive applications in photocatalysis, solar cells and photoelectrochemical (PEC) water splitting. [2] LaFeO3 has a suitable band gap of 2.07eV [3, 4] and exhibits excellent visible light photocatalytic performance. However, the poor charge transport and slow reaction kinetics at the surface [3, 4] are the main factors limiting its further improvement on photocatalytic application. To overcome these obstacles, transition metals (Mn, Co, Cu) are introduced into LaFeO3 and the photocurrent of 10% Cu doped sample is improved by three times than that of LaFeO3. The reduced charge transport resistance owing to the Fe3+ discharge is identified to benefit the PEC performance improvement after TM doping. On the other hand, the surface state of LaFeO3 is modified by electrodepositing of amorphous cobalt-phosphate (Co-Pi). It shows that the presence of Co-Pi down-shifts the onset potential by ~ 560 mV for anodic photocurrent and the improvement can be attributed to the enhanced water oxidation due to the CoII/CoIII-OH discharge on Co-Pi decorated layers. The transition anodic photocurrent is improved by about six times after Co-Pi coating under visible light at 0.50 V vs. Ag/AgCl and the electrochemical impedance spectroscopy certifies the enhanced charge transfer, which contributes to the meliorative anodic photocurrent. The incident photon-to-current conversion efficiencies of LaFeO3 can be promoted from 1.37% to 2.14% at 400 nm after Co-Pi coating. Our results demonstrate that modification of the electronic structure (TM doping) and surface state (Co-Pi coating) are the promising way to promote the photoconversion efficiency of LaFeO3-based PEC cells under visible light. References: X. Lu, S. Xie, H. Yang, Y. Tong, H. Ji, Chem. Soc. Rev., 43, 7581 (2014). Z. G. Yi and J. Ye, Appl. Phys. Lett., 91, 254108 (2007). K. M. Parida, K. H. Reddy, S. Martha, D. P. Das and N. Biswal, Int. J. Hydrogen Energy, 35, 12161 (2010). Q. Peng, B. Shan, Y. Wen and R. Chen, Int. J. Hydrogen Energy, 40, 15423 (2015).