Microstructure and Property of Laser Cladding Cobalt Based Alloy Coatings on Ductile Cast Iron
Tong Wenhui,Zhao Zilong,Wang Jie,Guo Xuming,Duan Xinhua,Liu Yu
DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16070039
2017-01-01
Abstract:In order to study the microstructure and property of cobalt based alloy layer cladding on the surface of ductile cast iron QT600-3 by laser, laser cladding of CoCrW alloy powder with the particle size of 46~106μm on the surface of QT600-3 was performed by 6 kW CO2 laser.Laser cladding process parameters were:laser power P=3.0 kW, scanning speed V=350 mm· min-1 , laser spot diameter 2 mm, lap ratio 1.5, three pass cladding, for which the thickness of cladding layer was about 3 mm.The temperature distri-bution of the cast iron sample was adjusted and controlled by the heat compensation during laser cladding processing.The microstruc-ture, composition, phases and hardness on the cross section of the cladding layer were investigated by Olympus metallurgical micro-scope ( OM) , Zeiss-Sigma scanning electron microscope ( SEM) , X′Pert MPD Pro X-ray diffraction ( XRD) and MHV2000 digital mi-cro hardness tester and the hardness changing was analyzed.The results showed that, the surface quality of the cladding layer was fine without crack, porosity and other defects;the cladding layer could be divided into melting zone, combined zone and heat affected zone, and it was integrated metallurgically with the ductile cast iron matrix, which was mainly composed ofγ-Co ( face centered cubic) solid solution and carbide of CoCx , Cr7 C3 , etc.The melting zone consisted of a surface layer of dendritic crystals and an internal layer of cellular crystals, and the transformation to the plate martensite occurred in the heat affected zone, where the globular graphite partially dissolved to the smaller graphite.The hardness of the cross section of the cladding layer increased rapidly and then increased gently with the increase of the distance from the surface of the graphite cast iron matrix, finally in the surface area rapidly increased.The maximum hardness of the cladding layer was HV0.21077, which was up to 4 times higher than that of the substrate of ductile cast iron.