Temperature-triggered fire warning PEG@wood powder/carbon nanotube/calcium alginate composite aerogel and the application for firefighting clothing

Yushu Wang,Jinru Liu,Yuhang Zhao,Yi Qin,Zhenyu Zhu,Zhicai Yu,Hualing He

DOI: https://doi.org/10.1016/j.compositesb.2022.110348

2022-12-01

Abstract:The design and exploitation of highly fire-safe aerogel with ultrasensitive fire-warning response and highly efficient thermal management capabilities are urgently needed to protect firefighters from burn injuries during fire operations and rescue. Herein, an ultralight temperature-triggered fire-warning aerogel composited of polyethylene glycol (PEG)@modified wood powder (MW)/amino-functionalized carbon nanotube (A-CNT)/calcium alginate (CA) (abbreviated as P@MW-A-CA) was fabricated. Benefiting the rapid decrease in electrical resistance of A-CNT at high temperatures, P@MW-A-CA achieved an ultrafast fire warning response time of ∼2.03 s when exposed to fire. Meanwhile, PEG was encapsulated into MW and acted as microtubule phase-change material (P@MW) in aerogel to effectively delay the heat penetration into P@MW-A-CA. The stiff MW served as the backbone endowed the fire-warning aerogel a “stiff-soft” structure that increased the mechanical resilience. P@MW-A-CA achieve flyweight density (0.038 g/cm3), low thermal conductivity (0.06233 ± 0.0012 W/m⋅K), and outstanding self-extinguishment (<1.02 s). This work provides an environmental friendliness approach to design an ultralight early fire-warning aerogel in firefighting clothing for enhancing the fire safety of firefighters.