The Influence of Core and Ring Power on the Formation of 5083 Aluminum Alloy Laser Weld Seam
Zhiyuan Yu,Guorong Zhu,Bo Xu,Hu Chen,Wenfei Chen,Chun Yu,Lei Jiang,Yunqi Ya,Jieshi Chen
DOI: https://doi.org/10.1007/s11665-024-09966-7
IF: 2.3
2024-01-01
Journal of Materials Engineering and Performance
Abstract:Flexible ring mode (FRM) laser technology effectively achieves high-speed and low-spatter laser welding. One of its critical applications is in power batteries, where the 5083 aluminum alloy is widely utilized due to its lightweight and high strength. However, there is still a gap in the influence of the power of the core and ring of the FRM on the weld forming of 5083 aluminum alloy and the mechanism of spatter suppression. This article uses laser confocal detection to examine the horizontal and numerical contours of the front and back welds. High-speed cameras were used to monitor and analyze the behavior of the molten pool and the mechanism of spatter formation. At the same time, a simulation of the welding temperature field was carried out for various process parameters. The behavior of the keyhole, molten pool, and spatter characteristics in pure Gaussian laser and FRM laser welding and the spatter suppression mechanism under FRM laser technology were revealed. The results found that the horizontal contour of the front weld seam has the highest contour height (534.24 µm) under pure Gaussian mode laser (4 kW + 0 kW), which is 3.7 times and 2.3 times higher than (3 kW + 1 kW) (113.62 µm) and (2 kW + 2 kW) (162.93 µm), respectively. When the center power remains 4 kW, as the ring power increases, the fusion width of the front weld seam increases, and the forming flatness improves. Under the same total power, FRM laser technology can increase the temperature of the molten pool, enhance the stability of high-temperature steam, and increase the opening area of small holes. As a result, it can reduce the escape speed of high-temperature steam, the driving force of the welding spatter, and the length of the liquid column. This study provides invaluable insights for engineering researchers on the utilization of shaping laser beams to prevent welding defects.