Aromatic P/N/Co-containing microsphere flame retardant for enhancing fire safety and mechanical properties of epoxy coating with lower curing temperature
Mingyu Ou,Richeng Lian,Jianhao Zhu,Rongjia Li,Jiahui Cui,Haocun Guan,Lei Liu,Chuanmei Jiao,Xilei Chen
DOI: https://doi.org/10.1016/j.porgcoat.2023.107728
IF: 6.6
2023-06-12
Progress in Organic Coatings
Abstract:Improving fire safety performance is one of the most important measures to expand the application field of epoxy resin (EP) coatings. In this work, a novel aromatic phosphorus/nitrogen/cobalt-containing microsphere flame retardant (FNP-Co) was synthesized via a solvothermal method and proposed for fabricating high-performance EP coatings. EP coatings containing FNP-Co exhibited not only remarkable fire safety performance but also enhanced mechanical properties and lower curing temperature. The differential scanning calorimetry (DSC) test demonstrated that FNP-Co endowed EP/FNP-Co coatings with lower curing temperatures compared with that of pure EP, which was conducive to the processing of EP coatings. Furthermore, with incorporating 4 wt% FNP-Co, the limiting oxygen index (LOI) of EP coating (EP/4FNP-Co) was increased to 30.2 %. And the peak heat release, peak smoke production, and peak CO production rate of EP/4FNP-Co were reduced by 19.85 %, 36.3 %, and 34.18 %, respectively, compared with those of pure EP. It has been found that FNP-Co promoted the formation of a honeycomb-like and compact char layer for EP/FNP-Co coatings during combustion, which could play a "labyrinth effect" and barrier effect to prohibit the heat and pyrolysis gas transfer. Moreover, the flexural strength and flexural modulus of EP/4FNP-Co were enhanced by 2.9 % and 32.5 % compared with those of pure EP. The unique microsphere structure and synergistic effect of ternary flame-retardant elements of FNP-Co were responsible for the desirable integrated properties of EP coatings. Therefore, this novel microsphere flame retardant can impart EP/FNP-Co coatings with a broad application in the coating field.
materials science, coatings & films,chemistry, applied