Abstract:Geological sequestration of CO2 in unminable coal seams is one of the effective ways to reduce greenhouse gas emissions and increase coalbed methane production. However, changes in the pore structure after CO2 injection may affect the mechanical properties of the coal reservoir, posing a challenge to the long-term safety of CO2 sequestration. Therefore, a proper understanding of the relationship between pore structure and mechanical properties of coal under CO2 treatment is essential. In this paper, Low-field nuclear magnetic resonance tests were carried out on bituminous coal after sub/super-critical CO2 (Sub-CO2/Sc-CO2) treatment, and uniaxial compression tests were used to analyze the mechanical properties and energy evolution of coal samples. The results demonstrate that the CO2 treatment increased the porosity and proportion of macropores, and the effect of Sc-CO2 treatment on the pore structure was more significant. Compared to the Sub-CO2 treated sample, the uniaxial compressive strength and elastic modulus decreased more in the Sc-CO2 treated sample, which may be related to the extraction capacity of Sc-CO2. Analysis of the energy evolution shows that more energy was converted into dissipated energy in the loading process of Sc-CO2 treated coal samples, which was used to form, expand and connect fractures. Moreover, the correlation between the rate of change in porosity and the rate of change in uniaxial compressive strength was 0.9579, indicating that changes in pore structure were the main cause of the change in the mechanical properties of coal. A conceptual model was proposed to explain the mechanism of the effect of the pore structure on the mechanical properties, and pressure selection during CO2 sequestration was discussed. Therefore, the results of this study are expected to provide references for the long-term safety assessment and injection pressure selection of CO2 sequestration.

Physical and Chemical Characteristics of Coal-binder Interface and Carbon Microstructure near Interface

Relationship between pore structure and mechanical properties of bituminous coal under sub-critical and super-critical CO2 treatment

Effect of binder composition on the preparation of formed coke with low-rank coal

Preparation of micro-porous monolithic activated carbon from anthracite coal using coal tar pitch as binder

Effect of Binders on the Crushing Strength of Ferro-Coke

The Effect of Oxygen Content in Binderless Cokes for High-Density Carbon Blocks from Coal Tar Pitch

Bonding Mechanism of Binder and Low-Rank Coal During Carbonization

Combustion and Emission Characteristics of Coal Logs with Different Binders for Transportation in a Hydraulic Pipeline

Pyrolysis mechanism of composite binder composed of coal tar pitch and phenolic resin for carbon materials

Nano-mechanical Properties and Pore-Scale Characterization of Different Rank Coals

Mesophase formation of coal-tar pitches used for impregnant of C/C composites

Research on the Slagging Characteristics of Blended Coals in A Pilot-Scale Furnace

Experimental study on physicochemical structure of different rank coals under acid solvent treatments and its effects on heat of gas adsorption

Relevance between various phenomena during coking coal carbonization. Part 4: Insight into the interaction of coal blending

Differences and correlations between microstructure and macroscopic properties of mesophase cokes derived from the components of high temperature coal tar pitch

Study of an Organic Binder of Cold-Bonded Briquettes with Two Different Iron Bearing Materials

Studies On The Coal-Powder Filled Polypropylene

Pore Characteristics and Slurryability of Coal Blends

An Atomic Force Microscopy Study of Coal Nanopore Structure

Study on Relationships between Coal Microstructure and Coke Quality during Coking Process

Effect of hydraulic binders on engineering properties of coal ash for utilization in pavement layers