Abstract:Abstract The present study aims to synthesised nano gold with chemical method with two shape sphere and rod with multi diameter and aspect ratio and then characterize the synthesised material with Atomic Force Microscope (AFM), Transmission Electron Microscope (TEM) and Ultraviolet-visible (UV–Visible ) spectrophotometer. The AFM and TEM characterization result of three samples for each sphere and rods show that the synthesised material are in nano range with diameter 31.9 nm, 36.19 nm and 79.37 nm respectively for nano sphere and diameters 39.9nm, 36.05 nm and 28 nm respectively for nano-rods samples and the UV-Visible spectrophotometer show that peak of surface plasmon resonance of nano-sphere are at wavelengths 532 nm, 535 nm and 546 nm and all are in the visible range and nano-rod have two peaks one in the visible range at wavelengths 525nm,518nm and 531nm and the other peak is in the near infrared range at wavelengths 633nm, 680nm and 875 nm respectively.

Nano Gold Spheres and Rods: Synthesis and Characterization