Abstract:Zn modified ZSM-5 zeolite supported Ni bifunctional catalysts were prepared by in-situ hydrothermal synthesis (Zn-Ni-ZSM-5), co-impregnation method (Zn-Ni/ZSM-5) as well as combining in-situ hydrothermal synthesis of Zn-ZSM-5 and sequential impregnation of Ni (Ni/Zn-ZSM-5) and used for the selective converting olefin to aromatics applicable for FCC gasoline hydro-upgrading. The Lewis (L) acid sites generated by ZnOH+ species and hydrogenation active sites from Ni0 species were varied with preparation method, in which their locations at the external surface or micropores of zeolite changed the acid properties of catalysts. Comparing to the Zn-Ni/ZSM-5 from the co-impregnation method, direct in-situ hydrothermal method could incorporate Zn and Ni species within zeolite, which makes the strong interaction between the metal species and the framework Al to form medium-strong L acids (ZnOH+/NiOH+). This leads to the decrease of ratio of Brønsted acid sites to L acid sites (B/L) from 0.40 to 0.12 and the difficulty in reducing of Ni cations to Ni0 from 57% to 30% Ni0 percent. Ni/Zn-ZSM-5 sample prepared by incorporating Zn species into micropores and sequential depositing Ni species at the external surface of zeolite possesses a low B/L ratio similar to Zn-Ni-ZSM-5 (0.20 versus 0.12) but a much higher Ni0 percent (52% versus 30%). Zn-Ni-ZSM-5 shows closer intimacy between Zn and Ni species comparing to Zn-Ni/ZSM-5 and Ni/Zn-ZSM-5. For the 1-hexene aromatization, the formed iso-alkene at acid sites was quickly saturated to iso-alkanes by the adjacent Ni0 particles over Ni-Zn-ZSM-5 catalyst in hydrogen steam. However, the location of aromatization active sites (ZnOH+, L acid sites) in micropores and hydrogenation active sites (Ni0 species) on external surface of Ni/Zn-ZSM-5 makes the tandem conversion of n-alkene → iso-alkene → aromatics, rather than the n-alkene → iso-alkene → iso-alkane. Thus, Zn-Ni-ZSM-5 with close intimacy of ZnOH+ and Ni0 particles shows a high iso-alkane selectivity (27.9% iC4 +), while Ni/Zn-ZSM-5 exhibits a high aromatics selectivity (39.6 %) in the conversion of 1-hexene in hydrogen steam. Similar results have also found in the conversion of n-heptane. Here, the control of the intimacy of Zn and Ni in ZSM-5 zeolites has been realized to be a good protocol to adjust the selective conversion of olefins/alkanes to aromatics versus iso-alkanes.

Effective factors on performance of zeolite based metal catalysts in light hydrocarbon aromatization

Effect of Metal on the Methanol to Aromatics Conversion over Modified ZSM-5 in the Presence of Carbon Dioxide

Effect of metal loading on catalytic activity and selectivity of ZSM-5 zeolite catalyst in conversion of methanol to olefins and aromatics

Influence of Channel, Construction and Brønsted Acid Sites on the Catalytic Conversion Pathways of Isobutane over MFI, TON and RFE Zeolites

Modified ZSM-5 Zeolite for Conversion of LPG to Aromatics

Study on direct aromatization reaction of methane: I. The reaction performance of supported Mo catalysts under oxygen-free conditions

Relay and Feedback Conversion Effect of Hydrocarbons between ZSM-5 Grains on Product Selectivity and Coke Formation during Methanol Aromatization

Utilization of Metal-Functionalized ZSM-5 for Methanol and Low-Carbon Hydrocarbon Coupling Aromatization

Modified zeolite ZSM-5 for the methanol to aromatics reaction

STUDY ON THE n-HEPTANE AROMATIZATION REACTION OVER ZSM-5 ZEOLITE CATALYSTS

Insights into the Key Factor of Zeolite Morphology on the Selective Conversion of Syngas to Light Aromatics over a Cr2O3/ZSM-5 Catalyst

Catalytic pyrolysis performance of alkanes to light olefins over bifunctional ZSM-5 zeolites

IMPROVED SELECTIVITY EFFECT OF COBALT, NICKEL CO-METAL IMPREGNATION WITH ZINC ON ZSM-5 FOR AROMATIZATION OF PROPANE:

Synthesis and consequence of Zn modified ZSM-5 zeolite supported Ni catalyst for catalytic aromatization of olefin/paraffin

Liquefied Petroleum Gas Aromatization to High Octane Gasoline over Zsm-5 Zeolite Catalyst at Low Temperature

Highly selective and stable Zn–Fe/ZSM-5 catalyst for aromatization of propane

Aromatization of Methanol over La/Zn/HZSM-5 Catalysts

Advances in the noble metal-zeolite catalysts for aromatic conversion

Isomorphous Substitution in ZSM-5 in Tandem Methanol/Zeolite Catalysts for the Hydrogenation of CO 2 to Aromatics

Improving the Hydrothermal Stability of ZSM-5 Zeolites in 1-Octene Aromatization by Sequential Alkali Treatment and Phosphorus Modification

Selective Conversion of Syngas to Aromatics over Metal Oxide/hzsm-5 Catalyst by Matching the Activity Between CO Hydrogenation and Aromatization