Factors Defining the Intercalation Electrochemistry of CaFe 2 O 4 -Type Manganese Oxides
Gene Nolis,José M. Gallardo-Amores,Jon Serrano-Sevillano,Evan Jahrman,Hyun Deog Yoo,Linhua Hu,Justin C. Hancock,Jannie Bolotnikov,Soojeong Kim,John W. Freeland,Yi-Sheng Liu,Kenneth R. Poeppelmeier,Gerald T. Seidler,Jinghua Guo,Miguel A. Alario-Franco,Montse Casas-Cabanas,Emilio Morán,Jordi Cabana,José M. Gallardo-Amores,Emilio Morán
DOI: https://doi.org/10.1021/acs.chemmater.0c01858
IF: 10.508
2020-08-31
Chemistry of Materials
Abstract:Oxides with the CaFe<sub>2</sub>O<sub>4</sub>-type structure have been predicted as being suitable hosts for reactions of intercalation of light cations such as Li and Mg because of their favorable cationic diffusion. Although Li has been shown to intercalate into the Mn<sub>2</sub>O<sub>4</sub> variant, the key structure property correlations determining function are not fully ascertained. This basic information is needed before attempting the intercalation of divalent cations, which face comparably higher migration barriers. For this purpose, the electrode function of CaFe<sub>2</sub>O<sub>4</sub>-type Li<sub>0.8</sub>Mn<sub>2</sub>O<sub>4</sub> was compared for materials made by a direct high-pressure route or through cation exchange from NaMn<sub>2</sub>O<sub>4</sub>. X-ray diffraction and absorption spectroscopy revealed that, despite having largely the same bulk structure, the presence of surface defects blocked Li<sup>+</sup> transfer in Li<sub>0.8</sub>Mn<sub>2</sub>O<sub>4</sub> made at high pressure. These defects were not present in the cation-exchanged material, which resulted in highly reversible Li intercalation with very fast kinetics in micrometric crystals. Delithiated electrodes from the cation-exchange synthesis were subsequently reduced in an ionic liquid electrolyte containing Mg<sup>2+</sup>. The process induced topotactic changes in the bulk, strongly suggesting the existence of intercalation, but it is accompanied by severe reactivity with the electrolyte that impedes reversibility. This study uncovers that defects affect the fundamentals of cation intercalation in this novel class of materials. The ability of the cation-exchanged material to conduct fast reactions with Li is consistent with calculated activation energy barriers and creates promise for their use as Mg hosts, provided that novel electrolytes enhanced stability at high potential can be realized.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.0c01858?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.0c01858</a>.XRD patterns, SEM images, EDX spectra, atomic percentages, crystallographic information from Rietveld refinements, crystal structure diagram, XAS spectra, derivative plots of XAS spectra, electrochemistry data, and images of postmortem cells (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.0c01858/suppl_file/cm0c01858_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical