Z‐Scheme 2D/2D Heterojunction of CsPbBr 3 /Bi 2 WO 6 for Improved Photocatalytic CO 2 Reduction
Yong Jiang,Hong‐Yan Chen,Jun‐Yan Li,Jin‐Feng Liao,Hong‐Hong Zhang,Xu‐Dong Wang,Dai‐Bin Kuang
DOI: https://doi.org/10.1002/adfm.202004293
IF: 19
2020-09-11
Advanced Functional Materials
Abstract:<p>Heterojunction engineering, especially 2D/2D heterojunctions, is regarded as a quite promising strategy to manipulate the photocatalytic performance of semiconductor catalysts. In this manuscript, a direct Z‐scheme 2D/2D heterojunction of CsPbBr<sub>3</sub>/Bi<sub>2</sub>WO<sub>6</sub> is designed and fabricated by a simple electrostatic self‐assembly process. By using ultrathin nanosheets with several atomic layers as the building blocks, a close CsPbBr<sub>3</sub>/Bi<sub>2</sub>WO<sub>6</sub> heterointerface over large area with quite a short charge transport distance is obtained, which enables a valid Z‐scheme interfacial charge transfer between Bi<sub>2</sub>WO<sub>6</sub> and CsPbBr<sub>3</sub> and thus boosts charge separation. The CsPbBr<sub>3</sub>/Bi<sub>2</sub>WO<sub>6</sub> heterojunction exhibits a superior photocatalytic performance toward CO<sub>2</sub> reduction. By incorporating Pt nanoparticles as the cocatalyst, a high photoelectron consumption rate of 324.0 µmol g<sup>−1</sup> h<sup>−1</sup> under AM 1.5G irradiation (150 mW cm<sup>−2</sup>) is obtained, which is 12.2 fold higher than that of CsPbBr<sub>3</sub> nanosheets. Moreover, a stable product yield of up to 1582.0 <b>µ</b>mol g<sup>−1</sup> and electron consumption yield of 8603.0 <b>µ</b>mol g<sup>−1</sup> for photocatalytic CO<sub>2</sub> reduction to CO (11.4%) and CH<sub>4</sub> (84.3%) can be achieved after 30 h of continuous catalytic reaction. The accelerated photogenerated charge transfer and spatial charge separation are investigated in detail by ultrafast spectra, photoelectrochemical test, and Kelvin probe force microscopy.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology