Packaging material-based polystyrene ZnFe2O4/clay nanocomposite: preparation, characterization and degradation studies

Wajeeha Saleem,Rabia Nazir,M. N. Chaudhry,Murtaza Saleem,Syed Hussain Abidi

DOI: https://doi.org/10.1007/s13204-021-02316-2

2022-01-14

Applied Nanoscience

Abstract:Polystyrene (PS) is one of the largely consumed polymeric materials that owing to its non-degradable nature have risen serious concerns about its disposal that is posing a great threat to mankind and environment. The present work deals with the synthesis of ZnFe2O4/Kaolinite (Fe–Zn/K) nanocomposite that when used as filler promotes self-degradation of PS under normal soil burial conditions. The films of post-consumer PS packaging material were prepared in lemon oil followed by incorporation of different levels of Fe–Zn/K (1–5%). The prepared materials were characterized using FT-IR, XRD, SEM/EDX, TGA, tensile and elongation studies. The results showed that increase in doping concentration strengthens the mechanical strength of the films. In addition to that, SEM/EDX indicates that with increase in ratio of Fe–Zn/K; the nanocomposite adopts different morphological formations. The incorporation of Fe–Zn/K into the polymer matrix also facilitates the degradation of PS films under normal soil burial conditions. The structural deformation of the PS films after 30 and 60 days of soil burial was evidenced by FT-IR and SEM/EDX. There was considerable reduction in temperature to 50% and 95% decomposition in each sample after burial which follows the order: t0 > t30 > t60. Similarly, there was considerable reduction in tensile strength and elongation in the all the samples after t30 and t60 again referring to structural deformation as a result of chemical changes in the films. All the studies pointed to self-degradation of the doped polymeric films with highest degradation achieved at 5% Fe–Zn/K loading but optimum degradation can be achieved at loading concentrations of 3% as well.

nanoscience & nanotechnology