Abstract:To explore the mechanical properties and fracture modes of basalt fiber-reinforced concrete, single-doped and hybrid-doped basalt fiber-reinforced concrete was prepared, and uniaxial failure tests under different basalt fiber-reinforced concrete contents were carried out. At the same time, the smooth kernel function in the traditional SPH method was improved, and the basalt fiber random generation algorithm was embedded in the SPH program to realize the simulation of the progressive failure of basalt fiber-reinforced concrete. The results show that under the circumstance with no basalt fiber, the specimen final failure mode is damage on the upper and lower surface, as well as the side edge, while the interior of the specimen center is basically intact, indicating that there is an obvious stress concentration phenomenon on the upper and lower surface when the specimen is compressed. Under the circumstance with basalt fiber, longitudinal cracks begin to appear inside the specimen. With the increase in the content, the crack location gradually develops from the edge to the middle, and the crack number gradually increases. This indicates that appropriately increasing the fiber content in concrete may improve the stress state of concrete, change the eccentric compression to axial compression, and indirectly increase the compressive strength of concrete. The numerical simulation results are consistent with the test results, verifying the rationality of the numerical simulation algorithm. For the concrete model without the basalt fiber, shear cracks are generated around the model. For the concrete model with basalt fiber, in addition to shear cracks, the tensile cracks generated at the basalt fiber inside the model eventually lead to the splitting failure of the model. The strength of concrete samples with basalt content of 0.1%, 0.2%, and 0.3% is increased by 1.69%, 5.10%, and 4.31%, respectively, compared to the concrete sample without basalt fiber. It can be seen that with the increase in the content of single-doped basalt fiber, the concrete strength is improved to a certain extent, but the improvement degree is not high; For hybrid-doped basalt fiber-reinforced concrete, the strength of concrete samples with basalt content of 0.1%, 0.2%, and 0.3% is increased by 14.51%, 15.02%, and 30.31%, respectively, compared to the concrete sample without basalt fiber. Therefore, compared with the single-doped basalt fiber process, hybrid doping is easier to improve the strength of concrete.

Compressive strength prediction of basalt fiber reinforced concrete via random forest algorithm

Mechanical Properties of SFRC: Database Construction and Model Prediction

Prediction Compressive Strength of Concrete Containing GGBFS using Random Forest Model

Prediction of the Mechanical Properties of Basalt Fiber Reinforced High-Performance Concrete Using Machine Learning Techniques

Analysis and prediction of compressive and split-tensile strength of secondary steel fiber reinforced concrete based on RBF fuzzy neural network model

The Prediction of Compressive Strength and Compressive Stress–Strain of Basalt Fiber Reinforced High-Performance Concrete Using Classical Programming and Logistic Map Algorithm

Predicting the Compressive Strength of the Cement-Fly Ash–Slag Ternary Concrete Using the Firefly Algorithm (FA) and Random Forest (RF) Hybrid Machine-Learning Method

Compressive Strength of Steel Fiber-Reinforced Concrete Employing Supervised Machine Learning Techniques

Experimental Study on Basic Mechanical Properties of Basalt Fiber Reinforced Concrete

Machine Learning Prediction Models to Evaluate the Strength of Recycled Aggregate Concrete

AN IMPROVED RANDOM FOREST MODEL TO PREDICT BOND STRENGTH OF FRP-TO-CONCRETE

Mechanical properties and meso-microscopic mechanism of basalt fiber-reinforced recycled aggregate concrete

Experimental Analysis of Bearing Capacity of Basalt Fiber Reinforced Concrete Short Columns under Axial Compression

Flexural Strength Prediction of Steel Fiber-Reinforced Concrete Using Artificial Intelligence

Machine learning models for predicting compressive strength of fiber-reinforced concrete containing waste rubber and recycled aggregate

Coupled Extreme Gradient Boosting Algorithm with Artificial Intelligence Models for Predicting Compressive Strength of Fiber Reinforced Polymer- Confined Concrete

Improvement of Computational Efficiency and Accuracy by Firefly Algorithm and Random Forest for Compressive Strength Modeling of Recycled Concrete

Designing a reliable machine learning system for accurately estimating the ultimate condition of FRP-confined concrete

Prediction of tensile strength of basalt continuous fiber from chemical composition using machine learning models

Investigating the Mechanical Characteristics and Fracture Morphologies of Basalt Fiber Concrete: Insights from Uniaxial Compression Tests and Meshless Numerical Simulations

Experimental study and mechanism analysis on basic mechanical properties of basalt fiber reinforced concrete