Structural engineering of nickel-coated carbon fibers with high electrical conductivity for flexible EMI shielding

Ayoub Darvishzadeh,Komeil Nasouri

DOI: https://doi.org/10.1007/s10854-022-07751-7

2022-01-19

Abstract:The structural engineering of carbon fibers (CFs) surface with mineral acid is a unique technique that increases oxygen-containing groups on sample surface leading to enhanced adhesion with the matrix but at the damage to the CFs leading to a reduction in application performance. The concentrated nitric acid (HNO3) treatment has to be for the optimum time to strike a balance between these opposite effects so that the nickel-coated carbon fibers (NCFs) will have the best combination of performance properties. Hence HNO3 treatment was employed to CFs for various time intervals (0–90 min). Four NCFs with untreated and HNO3-treated fabrics were manufactured and investigated for microstructure and electrical properties. It was observed that 60 min treatment time was the ideal one to achieve maximum possible enhancement properties. Nickel–Carbon adhesion was improved due to the inclusion of etched CFs surface and oxygen-containing functional groups as supported by scanning electron microscopic (SEM), Raman, and X-ray diffraction (XRD). The formation of nickel layer onto HNO3-treated CFs improved final properties, not only raising the electrical conductivity (201–421 S/cm) but also enhancing interfacial adhesion between nickel particles and CFs surface. The total shielding value with mainly the absorption mechanism of HNO3-treated NCFs increased up to + 42.9 dB over 8–12 GHz. These results indicated that acidic surface modification is an appropriate approach for the surface modification of CFs, high degree of adhesion between nickel and CFs, highly uniform nickel nanoparticles deposition, and development of high-performance shielding materials.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied