Mechanical and microstructural properties of additively manufactured Ti–6Al–4 V stents with CO2 laser postannealing treatment

Shih-Feng Tseng,Ting-Yuan Hung,Chun-Ming Chang

DOI: https://doi.org/10.1007/s00170-021-08381-9

IF: 3.563

2022-01-21

The International Journal of Advanced Manufacturing Technology

Abstract:Because of its excellent machining characteristics suited for fabricating complex and hollow three-dimensional components, additive-manufactured selective laser melting (SLM) technology has been increasingly applied in the production of medical implants. In this study, SLM combined with Ti–6Al–4 V powder was used to produce titanium alloy wires and vascular stents; various laser processing parameters were employed (laser average power and exposure time). A line-shaped CO2 laser postannealing treatment was used to improve the ductility of the Ti–6Al–4 V wires and stents. A universal testing system and a field-emission scanning electron microscope were used to compare the tensile strengths of the Ti–6Al–4 V wires, the compressive strength of the vascular stents, and the microstructural properties under various SLM parameters. The experimental results revealed the Ti–6Al–4 V wires fabricated using a laser power and exposure time of 100 W and 70 μs, respectively, to have the highest tensile strength (489.09 ± 15.27 MPa). Microtensile tests showed that the strain of the Ti–6Al–4 V wires annealed with the optimal laser power of 5 W increased from 1.18 ± 0.07 to 1.5 ± 0.41%. The compressive strength of the horizontal (S-2) structured stents before and after laser annealing was significantly higher than that of the circular arc (S-1) structured stents at both time points. The compressive strength of laser-annealed S-1 and S-2 structured stents was greater than that of unannealed stents. Compared with the unannealed stents, the compressive strength of the 5 W laser-annealed S-1 and S-2 structured stents was 58.9% and 124.4% higher, and the compression of S-1 and S-2 was 11.5% and 13.5% higher, respectively.

engineering, manufacturing,automation & control systems