Abstract:A novel method for fabricating shape-controlled and well-arrayed heterogeneous nanostructures by altering the melting point of the metal thin film at the nanoscale is proposed. Silver nanofilms (AgNFs) are transformed into silver nanoislands (AgNIs), silver nanoparticles (AgNPs), and silver nanogaps (AgNGs) that are well-ordered and repositioned inside the gold nanoholes (AuNHs) depending on the diameter of the AuNHs, the thickness of the AgNF, and the heating temperature (120–200 °C). This method demonstrates the ability to fabricate uniform, stable, and unique structures with a fast, simple, and mass-producible process. For demonstrating the diverse applicability of the developed structures, high-density AgNGs inside the AuNHs are utilized as surface-enhanced Raman spectroscopy (SERS) substrates. These AgNGs-based SERS substrates exhibit a performance enhancement, which is 1.06 × 10<sup>6</sup> times greater than that of a metal film, with a relative standard deviation of 19.8%. The developed AgNP/AgNI structures are also used as nonreproducible anti-counterfeiting signs, and the anti-counterfeiting/readout system is demonstrated via image processing. Therefore, our method could play a vital role in the nanofabrication of high-demand nanostructures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18122?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18122</a>.Low-magnification SEM images of the fabricated samples (Figure S1); SEM morphologies of the fabricated heterogeneous nanostructures depending on the heating temperature (120–200 °C) (Figure S2); the morphologies of heterogeneous nanostructures depending on the heating time from 1 to 20 min at an interval of 2 min (Figure S3); low- and high-magnification SEM images of the heterogeneous nanostructures fabricated on the 6 in. wafer (Figure S4); SEM images of the five different specimens fabricated using the same conditions (Figure S5); low- and high-magnification SEM images of the heterogeneous nanostructures before and after peel test (Figure S6); SEM images of the fabricated well-aligned nanostructures with various shapes (Figure S7); Raman signal of the R6G molecule on the nine different points of the same substrate (Figure S8); results of long-term stability test for anti-counterfeiting applications (Figure S9) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18122/suppl_file/am0c18122_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Highly Improved Fabrication of Ag and Al Nanostructures for UV and Nonlinear Plasmonics

Colloidal Synthesis of Crystalline Aluminum Nanoparticles for UV Plasmonics

Fabrication of Alloyed Plasmonic Nanostructures

Low temperature annealing method for fabricating alloy nanostructures and metasurfaces: Unlocking a novel degree of freedom

Single-crystalline Aluminum Nanostructures on Semiconducting GaAs Substrate for Ultraviolet to Near-infrared Plasmonics

Stabilization of Plasmonic Silver Nanostructures with Ultrathin Oxide Coatings Formed Using Atomic Layer Deposition

The Fabrication and Optical Property of Silver Nanoplates with Different Thicknesses.

Carbon‐Assisted Stable Silver Nanostructures

Galvanic Replacement Reaction to prepare nanoporous Aluminum for UV plasmonics

Template-free Fabrication of Ag Nanowire Arrays/al2o3assembly with Flexible Collective Longitudinal-Mode Resonance and Ultrafast Nonlinear Optical Response

Scalable, Green Fabrication of Single-Crystal Noble Metal Films and Nanostructures for Low-Loss Nanotechnology Applications

Silver high-aspect-ratio micro- and nanoimprinting for optical applications

Fabrication of Centimeter-Scale Plasmonic Nanoparticle Arrays with Ultranarrow Surface Lattice Resonances.

Shape-Controlled and Well-Arrayed Heterogeneous Nanostructures via Melting Point Modulation at the Nanoscale

Fabrication and Optical Spectral Characterization of Linked Plasmonic Nanostructures and Nanodevices

Fully alloyed Ag/Au nanorods with tunable surface plasmon resonance and high chemical stability.

Highly Controllable Fabrication of Gold Composite Nanostructures by Multiple Electroplating for High‐Performance Electrochemical and Raman Scattering Measurements

Direct Electron Beam Writing of Silver-Based Nanostructures

Ultraconfined plasmons in atomically thin crystalline silver nanostructures

Controlling and monitoring laser-mediated localized synthesis of silver nanoparticles within gold nanoapertures

Fabrication of Ag@SiO2@Y2O3: Er nanostructures for bioimaging: Tuning of the upconversion fluorescence with silver nanoparticles