Abstract:Journal of Composite Materials, Ahead of Print. In fabric-cement composites, the limited impregnation of cementitious matrix products due to thick and twisted yarns leads to premature failure due to poor bonding strength. In addition, cellulosic textile reinforcements have many challenges about durability, appearance of voids at mortar-fiber interface, and rise of microcracks. Textile performances were evaluated in different conditions: coated with micro-silica powder, pretreated, and without any treatment. This study also assessed how textile weave structure and yarn geometry configuration affect the interactions of two different jute textiles (Close Weave Jute Fabric – CJF and Open Weave Jute Fabric - OJT) when used as reinforcement in mortar matrix. Textile characterization and composite analysis (by four-point bending tests, SEM/EDS, and physical tests) were conducted to assess the different textile reinforcements, the mechanical behavior of produced composites, and visual and chemical compounds analysis of the interfacial transition zone between textile and mortar matrix after silica coating. Micro silica powder coating was deemed necessary to address limited impregnation and to avoid telescope pull-off. Weave structure determined the difference between jute fabrics to reinforce mortar matrix, being only OJF (larger interstices in the weave structure) with micro silica coating allowed a better matrix interaction and stood out from the other textiles and achieved the best specific energy of all samples, (4.28 ± 0.91) kJ.m-2. Calcium and silicon inside the yarn interstices and textile-matrix interface indicate the formation of strong bonds by calcium-silicate-hydrate products. The silica coating treatment enhanced formation of strong bonds, which demonstrated future promise for natural fiber application.

Enhancement of fabric–mortar interfacial adhesion by particle decoration: insights from pull-off measurements

Uniaxial Tensile Behavior of Anchored Carbon Fabric-Reinforced Cementitious Matrix Plates

Jute textiles with enhanced interfacial bonding as reinforcement for cementitious composites

Fabric-Reinforced Cementitious Matrix (FRCM) Carbon Yarns with Different Surface Treatments Embedded in a Cementitious Mortar: Mechanical and Durability Studies

Pull-Out Performance of Anchored Carbon-Fiber Bundles in Cementitious Matrix

Practical Method of Improving Bonding Behavior Between Fiber Textile and Mortar

Influence of Electrophoretic Deposition of Micro- or Nanosized Silica Particles on the Microstructure of Carbon Fibers and Their Bond Behavior with Cementitious Matrices

Influence of Cementitious Material Infiltration on Piezoresistive Effect of Carbon Fiber Bundle

Bond Characteristics of Carbon, Alkali Resistant Glass, and Aramid Textiles in Mortar

Improved Interfacial Bonding Strength and Reliability of Functionalized Graphene Oxide for Cement Reinforcement Applications

Reinforcement Effect and Mechanism of Carbon Fibers to Mechanical and Electrically Conductive Properties of Cement-Based Materials

Bio-Inspired Impregnations of Carbon Rovings for Tailored Bond Behavior in Carbon Fiber Reinforced Concrete

Interfacial Microstructure and Bond Strength of Nano-Sio2-coated Steel Fibers in Cement Matrix

Bond Investigation Of Hybrid Textile With Self-Compacting Fine-Grain Concrete

Enhancement of strength and ductility of cement-based composites by incorporating silica nanoparticle coated polyvinylalcohol fibers

Mechanical Performance of Cementitious Materials Reinforced with Polyethylene Fibers and Carbon Nanotubes

Synergistic Effect of Carbon-Based Reinforcements on the Mechanical Properties of Cement-Based Composites

Experimental Study on Improvement of Interfacial Bond Properties of Carbon Fiber Reinforced Cement Matrix Composites by Nano Silica

Nano silica grafted on modified polyacrylonitrile fiber improves the interfacial strength of fiber‐reinforced concrete

Effects of Halloysite-Decorated Basalt Fiber on Mechanical Properties and Microstructure of Iron Tailings-Based Cementitious Mortar

Carbon Fiber Surface Nano-Modification and Enhanced Mechanical Properties of Fiber Reinforced Cementitious Composites