Abstract:In this paper, a process of selective extraction and separation of vanadium (IV) from acid leaching solution of spent oil hydrotreating catalyst by a solvent extraction method with P204 as an extractant was proposed. Because the leaching solution contained a large amount of elements such as nickel, aluminium and iron, the effects of various conditions on the separation of vanadium from nickel, aluminium and iron were investigated and the optimum conditions were determined. At the same time, the thermodynamic discussion on the extraction process of vanadium in the system was carried out. Using kerosene as a diluent and 20% (v/v) P204 as an extractant, the single-stage maximum extraction ratio of 93.47% for vanadium was obtained under the optimum extraction conditions of O/A ratio of 2, oscillation time of 8 min, extraction temperature of 298 k(25 °C) and pH value of initial aqueous phase of 2. After three stages of countercurrent extraction experiments, the concentration of vanadium, iron, nickel and aluminium in the loaded organic phase were 0.377, 0.001, 0.005 and 0.02 g/L, respectively, and their extraction ratios were determined to be 99.21%, 1.02%, 2.857% and 1.942%, respectively, realizing the selective extraction and separation of vanadium. With 2 mol/L of sulfuric acid as a stripping reagent, the complete removal of vanadium from the loaded organic phase could be achieved at O/A ratio of 2 by three stages of countercurrent experiments of vanadium removal. The thermodynamic calculation showed that the enthalpy change of the vanadium extraction in the system was −20.37 kJ.mol−1. This demonstrated that the extraction of vanadium from acid leaching solution of spent oil hydrotreating catalyst with P204 as the extractant was an exothermic reaction.

Selective Extraction of Tungsten(VI) with 4-methyl-2-pentanol from Hydrochloric Acid Media

Selectively extracting H 2 WO 4 of high purity from the H 2 SO 4 decomposition product of scheelite through hydrogen peroxide coordination followed by purification using ion-exchange and solvent extraction and thermal decomposition

Extraction and separation of tungsten from acidic high-phosphorus solution

Removal and Recovery of Arsenic(III) from Hydrochloric Acid Leach Liquor of Tungsten Slag by Solvent Extraction with 2-Ethylhexanol

Separation of Vanadium and Tungsten in Roasting‐acid Leaching Solutions of the Spent Selective Catalytic Reducing Denitration Catalyst by Co‐extraction Using Hydroxyoxime Extractant‐quaternary Ammonium Salt Extractant LIX984–N263 Extractant

Liquid-Liquid Extraction of Vanadium(V) and Niobium(V) with Tris(2-ethylhexyl)phosphate: Mutual Separation of Vanadium(V), Niobium(V), and Tantalum(V), and Analysis of Steel Samples

Extraction chromatography with bis(2-ethylhexyl)phosphoric acid for separation of tin(IV)

Solvent Extraction of Molybdenum (VI) from Hydrochloric Acid Leach Solutions Using P507. Part I: Extraction and Mechanism

Analytical Separation of Gold(III) by Extraction with 4-Methyl-2-pentanol from Hydrochloric Acid Media

Highly efficient and selective removal of vanadium from tungstate solutions by microbubble floating-extraction

Complexation extraction of scheelite and transformation behaviour of tungsten-containing phase using H2SO4 solution with H2C2O4 as complexing agent

Sustainable Selective Recovery of Sulfuric Acid and Vanadium from Acidic Wastewater with Two-Step Solvent Extraction

Solvent Extraction Separation of Niobium(V), Tantalutn(V) or Titanium(IV), and Vanadium(V) by 2′-Hydroxy-4-methoxy-5′-methyl Chalkone Oxime (HMMCO) from Their Binary Mixtures

Die Extraktion von Vanadin mit 4-Methyl-2-pentanol

Selective and Efficient Photoextraction of Aqueous Cr(VI) As a Solid-State Polyhydroxy Cr(V) Complex for Environmental Remediation and Resource Recovery.

The Extraction of Tc(VII), Fe(III), Ru(II), Pd(II) and Mo(VI) from Nitric Acid Solution by Bis(2,4,4-trimethylpentyl)dithiophosphinic Acid (HBTMPDTP)

Direct Tungsten Extraction from Scheelite in a Molten Salt Media

Extraction and stripping of Cr(VI) from aqueous solution by solvent extraction

Recovery of vanadium from acid leaching solutions of spent oil hydrotreating catalyst using solvent extraction with D2EHPA (P204)

Separation of V (V) and Mo (VI) in roasting-water leaching solution of spent hydrodesulfurization catalyst by co-extraction using P507 - N235 extractant

Extraction of Palladium(II) with 4-[(Hexylsulfanyl)methyl]-3,5-dimethylisoxazole from Hydrochloric Acid Solutions