Synthesis of nanophase hydroxyapatite/collagen composite
R. Z. Wang,F. Z. Cui,H. B. Lu,H. B. Wen,C. L. Ma,H. D. Li
DOI: https://doi.org/10.1007/BF00665911
1995-01-01
Journal of Materials Science Letters
Abstract:One of the most important objectives in biomaterials science is the development of new materials for bone substitution. It has been found that hydroxyapatite (HAp), which is the most widely studied bioceramic, has an excellent biocompatibility and a certain degree of bioactivity [1, 2]. However, HAp is limited in its use because it is brittle compared with natural bone. In order to improve the toughness and bioactivity of bone substitution materials, biocomposites made of HAp and biocompatible organic components or bioactive glass have been developed in recent years [3-10]. Among these materials, HAp/collagen composite is of special interest because it mimics the composition of natural bone [7-10]. Preliminary study reveals that this composite has a better osteo-inductive capacity in cell culture than monolithic HAp [9]. So far, HAp/collagen composite is still at the initial stage of development. It is well known that HAp is nanometre sized and deposits in an orderly way on the collagen matrix in natural bone. However, with the synthetic methods reported, it is not easy to obtain either a uniformly mixed composite [7], or a fine crystal sized material [8-10], while these two factors are important to the bioactivity of the composite [2]. Therefore, new methods are needed to obtain an HAp/collagen composite which mimics not only the composition but also the microstructure of natural bone. This letter reports a new preparation method of HAp/ collagen composite in which nanometre sized HAp is homogeneously dispersed in collagen matrix. The results of biological testing will be published separately. Commercially purchased HAp powder and type 1 insoluble collagen from bovine achilles tendon were used as starting materials. Firstly, i g HAp was dissolved in 150 ml, 0.1 N HC1 at 20 °C and 450 mg type i collagen was added to the solution, which was then ultra-sonicated, using a Model Gl125 ultrasonator, until a thoroughly mixed slurry was obtained. Secondly, this solution was diluted to 2000 ml with distilled water, and 23.376 g NaC1 was added to increase the stability of the calcium containing solution [11]. This resulted in a 5 mM calcium solution with pH 3.0. At the third step, the solution was gently stirred at 20 °C, and 0.05 M potassium hydroxide solution was added in drops to the calcium solution to adjust the pH to 7.4. When the pH exceeded about 7.0, the solution became supersaturated and HAp started to precipitate onto the collagen. The solution was maintained at pH 7.4 for 10 min, after which the composite was harvested by centrifugation at 5000 rpm and freeze-dried. The