Structures, Microstructures, Properties, and Applications of TiAl Alloys
Zite Wang,Gong Zheng,Zhixiang Qi,Yang Chen,Hao Xu,Henggao Xiang,Guang Chen
DOI: https://doi.org/10.1360/tb-2023-0037
2023-01-01
Abstract:Lightweight aerospace weapons and equipment are a major strategic need for China. Weight reduction of key components of aero engines can improve the thrust-to-weight ratio and reduce energy consumption while also lowering costs and bringing direct economic benefits. Currently, the core hot-end components of aero engines primarily comprise nickel-based superalloys with high density, which restricts technological innovation and progress in the aerospace field to a certain extent. Thus, the development of novel, lightweight structural materials is critical. With a theoretical density of only 3.9 g/cm(3), which is less than half that of nickel-based superalloys, and a higher melting point, TiAl intermetallic compounds have attracted considerable attention for aerospace applications owing to their excellent lightweight and heat-resistant properties. First, this review briefly describes the crystal structures of the main phases and phase diagrams of TiAl alloys. TiAl alloys comprise two basic phases:.-TiAl with an L10-type ordered face-centered tetragonal structure and alpha 2Ti3Al with a D0(19)-type ordered close-packed hexagonal structure. With increasing temperature, the disordered close-packed hexagonal a-phase continues to undergo a phase transformation into the disordered body-centered cubic structure beta-phase. By adding a certain amount of beta-phase stabilizing elements to the TiAl alloy, the high-temperature beta-phase can be retained until 25 degrees C, but its crystal structure will transform from disordered to ordered body-centered cubic structure beta(o) phase. Further, the shear of the beta(o) phase along the <111> direction yields the ordered. phase of the hexagonal structure. Another common precipitated phase in TiAl alloys is the Ti2AlNb phase, which has an ordered orthorhombic structure (also known as the O phase) and is mainly produced from the alpha(2) phase. In addition, phase diagrams of high Nb-TiAl and TNM alloys are shown as sample examples. Furthermore, this review focuses on the microstructures and properties of several TiAl alloys. The four typical microstructures, unique banded microstructures, and polysynthetic twinned TiAl single crystals are shown. Mechanical properties of TiAl alloys, such as Ti-48Al-2Cr-2Nb, TNM, and high Nb-TiAl alloys, are also demonstrated. Current applications of TiAl alloys fabricated using different methods in different fields are presented, such as low-pressure turbine blades manufactured using casting, forging, and three-dimensional printing; engine turbochargers; and engine connecting rods and exhaust valves. Finally, future development and application prospects of TiAl alloys are discussed, including developing processing techniques for TiAl alloys, establishing durability and damage tolerance prediction methods for TiAl alloys, developing joining processes between TiAl and TiAl alloys or other dissimilar materials, and developing new TiAl alloys.