Abstract:Alkali-silica reaction (ASR) and expansion induced are one of the major concerns over durability of concrete structures. It causes an increase in internal stresses and hence deteriorating mechanical properties, reducing load capacity, and compromising structures' serviceability. Factors governing ASR include water-to-cement ratio, alkali content, the content of reactive aggregate, exposure temperature, relative humidity, etc. Previous prediction models for ASR expansion focus on the measurements under particular conditions and these models are suffering from the neglect of effects of some factors. This study aims to propose a back-propagation neural network (BPNN) model to predict ASR by considering both mix compositions and environmental conditions. In this paper, by adopting two different training functions, namely Levenberg-Marquardt function (LM) and Bayesian regularisation backpropagation (BR), two models of LM-BPNN and BR-BPNN were developed and proposed. To achieve this, a database containing 168 pairs of data from 25 studies was established, its data includes water-to-cement ratio, cement content, alkali fraction, content of non-reactive and reactive fine/coarse aggregate, temperature, and relative humidity. Results indicate that both LM-BPNN and BR-BPNN models can produce reasonable estimates for ASR expansion at 180 days with MSE and R of 0.00209%, 0.002753%, 0.926 and 0.912, respectively. Results reveal that fraction of reactive fine/coarse aggregate is dominant on ASR expansion while alkali content and humidity have a significant correlation with expansion. Water-to-cement ratio, cement content, and content of non-reactive fine/coarse aggregate have low impact on ASR expansion based on the results.

Calculation of alkali silica reaction (ASR) induced expansion before cracking of concrete

Comparison of Field Observations with Laboratory Test Results on Concretes Undergoing Alkali-Silica Reaction

Analytical and experimental studies on alkali-silica reaction mechanism: Aggregate cracking and chemical composition change of gel

Meso-scale finite element modeling of Alkali-Silica-Reaction

Chemo-Mechanical Model for the Expansion of Concrete Due to Alkali Silica Reaction

Concrete Expansion Induced by Alkali–Silica Reaction in a Small Arch Dam

Alkali-silica reaction expansion model for confined concrete with stress-dependency and casting direction anisotropy

Failure criteria and microstructure evolution mechanism of the alkali–silica reaction of concrete

Correlating alkali-silica reaction (ASR) induced expansion from short-term laboratory testings to long-term field performance: A semi-empirical model

Kinetics of Alkali-Silica Reaction: Application to Sandstone

Modeling of alkali-silica reaction in concrete: a review

Effects of temperature on expansion of concrete due to the alkali-silica reaction: A simplified numerical approach

Time-dependent Effect of Expansion due to Alkali-silica Reaction on Mechanical properties of Concrete

Prediction of Service Life of Concrete Structures Affected by Alkali-Silica Reaction

Development of prediction models for evaluation of alkali-silica reaction in concrete

Experimental and numerical study of long-term alkali-silica reaction (ASR) expansion in mortar with recycled glass

Model for alkali-silica reaction expansions in concrete using zero-thickness chemo-mechanical interface elements

Effect of ASR related expansion in the concrete due to alkali concentration and total amount of alkali

Predicting damage in aggregates due to the volume increase of the alkali-silica reaction products

Alkali silica reaction in concrete - Revealing the expansion mechanism by surface force measurements

Modeling Alkali-Silica Reaction Using Image Analysis and Finite Element Analysis