Abstract:A novel hydrogenated nitrile rubber (HNBR) composite filled with organically modified Al2O3 nanoparticle was fabricated. The effects of the nano‐Al2O3 with different particle sizes on the curing, mechanical, and tribological properties of the HNBR composites were studied. The results indicate the curing, mechanical, and tribological properties of the HNBR composites were improved for the addition of nano‐Al2O3, and the smaller nano‐Al2O3 size was, the more obvious the effect was. The HNBR composite filled with 10 nm nano‐Al2O3 had the better mechanical properties and anti‐wear performance due to that the 10 nm nano‐Al2O3 could form denser cross‐linked network. A novel hydrogenated nitrile butadiene rubber (HNBR) composite filled with organically modified Al2O3 nanoparticle was fabricated. The effects of nanoparticle Al2O3 (nano‐Al2O3) with different particle sizes on the curing, mechanical, and tribological properties of the HNBR composites were studied. Nano‐Al2O3 with different particle sizes (i.e. 10, 50, 100, and 200 nm) was filled into the HNBR in this work. Attenuated total reflection Fourier transform infrared (ATR‐FTIR) spectroscopy was used to investigate the degree of grafting between modified nano‐Al2O3 and rubber matrix. Universal material testing machine was used to study the mechanical properties of the HNBR composites. The tribological properties of the HNBR composites were tested by a ballon‐on‐disk tribometer. The wear morphology of the HNBR composite surface was examined by scanning electron microscopy (SEM). The test results reveal that the nano‐Al2O3 as filler of HNBR composite promoted the vulcanization process, improved tensile and compressive strength, and increased hysteresis energy density and the damping coefficient. And the mechanical properties of the HNBR composite improved gradually with the decrease of nano‐Al2O3 particle size. The friction and wear test results show that the addition of nano‐Al2O3 greatly reduced the dry friction coefficient and specific wear rate of HNBR composites, and the friction coefficient and wear rate decreased gradually with the decrease of nano‐Al2O3 size. The HNBR composite filled with 10 nm nano‐Al2O3 had the better mechanical properties and anti‐wear performance due to that the 10 nm nano‐Al2O3 could form denser cross‐linked network.

Homogeneous Hydrogenation Art of Nitrile Butadiene Rubber: A Review

Design Strategies and Structure-Performance Relationships of Heterogeneous Catalysts for Selective Hydrogenation of 1,3-Butadiene

Direct Hydrogenation of Nitrile Butadiene Rubber Latex Using M41 Catalyst

Hydrogenation of Carboxyl Nitrile Butadiene Rubber Latex Using a Ruthenium-Based Catalyst

Diimide-Mediated Hydrogenation of Nitrile Butadiene Rubber

Enhanced catalytic performance of Pd-Pt bimetallic alloy nanocatalyst for hydrogenation of nitrile butadiene rubber

Hydrogenation of olefinic bonds in nitrile butadiene rubber on single-atom Pd 1 /CeO 2−x catalysts with ultrahigh mass activity and stability

Nitrile Butadiene Rubber Hydrogenation over a Monolithic Pd/CNTs@Nickel Foam Catalysts: Tunable CNTs Morphology Effect on Catalytic Performance

Highly dispersed Pd nanoclusters anchored on CNx-modified SiO2 for selective hydrogenation of nitrile-butadiene rubber

Selective hydrogenation of nitrile butadiene rubber latex using Catmetium®RF 4 catalyst

Regulating the Electronic Structure of Pd Nanoparticles on NH3‐pretreated Nano‐flake TiO2 for Efficient Hydrogenation of Nitrile Butadiene Rubber

Hydrogen Permeation Behavior and Mechanisms in Nitrile Butadiene Rubber Composites for Hydrogen Sealing

Research progress of blending modification of hydrogenated acrylonitrile butadiene rubber

Preparation of diene-based nanoparticles by semibatch microemulsion polymerization and their catalytic hydrogenation

Preparation of Poly(Butadiene–Styrene–Vinyl Pyridine)/Poly(Acrylonitrile–Butadiene) Core–Shell Nanoparticles by Intermittent Seeded Emulsion Polymerization and Their Catalytic Latex Hydrogenation

Intrinsic challenges and strategic approaches for enhancing the potential of natural rubber and its derivatives: A review

Research on Mechanical Properties, Compatibility, Flame Retardancy, Hot-Air Ageing Resistance of Hydrogenated Nitrile-Butadiene Rubber/Chloroprene Rubber Blends

Synthesis of Low Temperature Resistant Hydrogenated Nitrile Rubber Based on Esterification Reaction

Heterogeneous hydroformylation of alkenes by Rh-based catalysts

Facile fluorination of nitrile-butadiene rubber via olefin cross metathesis

Curing, mechanical, and tribological properties of hydrogenated nitrile butadiene rubber reinforced with Al2O3 nanoparticles