Abstract:Porous separators are essential for alkaline electrochemical energy technologies, such as alkaline water electrolyzers (AWEs). These separators are promising alternatives to dense membranes because they offer the potential for low cost and high ionic conductivity. However, two significant challenges in developing efficient and durable alkaline energy systems are the suppression of hydroxide ions-induced degradation and the reduction of gas permeation in porous separators. Compared to hydrophobic polysulfone (PSF), KOH-doped poly (oxindole biphenylene) (POBP) is a highly stable ion-solvating polymer that can conduct both potassium and hydroxide ions. Building upon this, a series of porous separators based on POBP polymer with different zirconia loads were designed using NIPS to investigate the chemical stability and water electrolysis performance where the Z60 separator exhibits remarkable characteristics, including low area resistance (0.227 Ω cm 2 ), high bubble point pressure (0.813 MPa), low H 2 permeability (0.5 L min −1 ·cm −2 ) and exceptional 5040 h of ex-situ durability in 6 M KOH at 80 °C. Furthermore, the Z60 diaphragm showed a higher breaking time and lower weight loss after 261 h at 80 °C in the Fenton reagent, with the remaining mass being Z60 was 38 %. Notably, the Z60 diaphragm, when equipped with Ni–Al catalysts, achieved a current density of 0.5 A/cm 2 at 1.7 V, which surpasses that of Zirfon (0.5 A/cm 2 at 1.8 V). More importantly, when using Ni foam catalysts, the Z60 diaphragm demonstrated stable operation under 0.125 and 0.5 A/cm 2 current densities at 80 °C for more than 900 h and 1200 h, significantly improving the durability of the porous separators. The results of this study showed that the blending of POBP can lead to the development of highly chemically stable porous diaphragms, thereby opening up a new avenue for advanced AWEs.

Polysulfone and zirconia composite separators for alkaline water electrolysis

High chemical stability poly(oxindole biphenylene)/ZrO 2 porous separator for alkaline water electrolysis

Highly Efficient Alkaline Water Electrolysis Using Alkanolamine-Functionalized Zirconia-Blended Separators

Zirconia Toughened Alumina-Based Separator Membrane for Advanced Alkaline Water Electrolyzer

Diaphragm and membrane for alkaline water electrolysis with zirconium hydroxide hydrogel as hydrophilic filler

An Expanded Clay-Coated Separator with Unique Microporous Structure for Enhancing Electrochemical Performance of Rechargeable Hybrid Aqueous Batteries

Polysulfone-Based Anion-Exchange Membranes for Alkaline Water Electrolyzers

Enhanced Mechanical Behavior and Electrochemical Performance of Composite Separator by Constructing Crosslinked Polymer Electrolyte Networks on Polyphenylene Sulfide Nonwoven Surface

High-Performance Composite Membranes: Embedding Yttria-Stabilized Zirconia in Polyphenylene Sulfide Fabric for Enhanced Alkaline Water Electrolysis Efficiency

Suppression Of Polysulfide Shuttling With A Separator Modified Using Spontaneously Polarized Bismuth Ferrite For High Performance Lithium-Sulfur Batteries

Fabrication and Investigation of PE-SiO2@PZS Composite Separator for Lithium-Ion Batteries

Preparation and Performance of Silica/polypropylene Composite Separator for Lithium-Ion Batteries

Separators and Membranes for Advanced Alkaline Water Electrolysis

Thermally Stable, Nano-Porous and Eco-Friendly Sodium Alginate/attapulgite Separator for Lithium-Ion Batteries

Cellulose/Polysulfonamide Composite Membrane as a High Performance Lithium-Ion Battery Separator

Zincate-Blocking-Functionalized Polysulfone Separators for Secondary Zn-MnO2 Batteries

In situ covalent crosslinking strategy to construct highly stable composite separators for lithium-ion batteries

Lithium ion battery separators: Development and performance characterization of a composite membrane

Separators with Biomineralized Zirconia Coatings for Enhanced Thermo- and Electro-Performance of Lithium-Ion Batteries.

Effect of Al2O3/SiO2 Composite Ceramic Layers on Performance of Polypropylene Separator for Lithium-Ion Batteries

Effect of Silica/Polyvinyl Alcohol Porous Layers on Performance of Polypropylene Separators for Lithium ion Batteries