Packaging Composite Films Fabricated from Cellulose Pulp with Polyurethane and Curcumin by Using NMMO ionic Liquid Solvent

Chaehyun Jo,Sam Soo Kim,Srinivasan Ramalingam,Prabakaran D. S,Balasubramanian Rukmanikrishnan,Jaewoong Lee

DOI: https://doi.org/10.21203/rs.3.rs-1063688/v1

2021-11-23

Abstract:Abstract Cellulose pulp (CP), polyurethane (PU), and curcumin-based biocompatible composite films were prepared using a simple cost-effective method. These materials dissolved well in the ionic liquid solvent N-methylmorpholine N-oxide. Significant structural and microstructural changes were observed in CP upon the addition of PU. These changes were studied using Fourier transform infrared spectroscopy, X-ray diffraction, and scanning electron microscopy. The 5% and 10% gravimetric losses of the CP/PU/curcumin composite were found to be in the range 87.2–182.3 oC and 166.7–249.8 oC, respectively. The addition of PU significantly improved the thermal stability and water barrier properties of the composites. All the composites exhibited single T g values in the range 147.4–154.2 oC. The tensile strength of CP was measured to be 93.2 MPa, which dropped to 14.1 MPa for the 1:0.5 CP/PU composite and then steadily increased to 30.5 MPa with further addition of PU. The elongation at break of the composites decreased from 8.1 to 3.7% with the addition of PU. The addition of PU also improved the water vapor permeability (3.96 ×10 –9 to 1.75 ×10 –9 g m –1 s –1 Pa –1 ) and swelling ratio (285 to 202%) of the CP composite films. The CP/PU/curcumin composite exhibited good antioxidant activity and no cytotoxicity when tested on the HaCat cell line. The visual appearance and UV transmittance (86.2–32.9% at 600 nm) of the CP composite films were significantly altered by the incorporation of PU and curcumin. This study demonstrates that CP/PU/curcumin composites can be used for various packaging and biomedical applications.