Temperature and Time Relaxation of the Complex Young’s Modulus for Isotropic and Uniaxially Drawn Polymers

S. V. Bronnikov

DOI: https://doi.org/10.1007/978-3-642-51062-5_209

1998-01-01

Abstract:The mechanical behavior of an idealized linear polymer has been described in the term of the generalized Maxwell relaxation theory by Tobolsky and Eyring (1943). They have resulted the following equations for both storage (E′) and loss (E″) elastic moduli as functions of frequency1$${\text{E}}'\left( \omega \right) = \int\limits_{ - \infty }^{ + \infty } {{\text{H}}\left( \tau \right)\frac{{\omega ^2 \tau ^2 }}{{1 + \omega ^2 \tau ^2 }}{\text{d}}\left( {\ln \tau } \right)}$$and2$${\text{E}}''\left( \omega \right) = \int\limits_{ - \infty }^{ + \infty } {{\text{H}}\left( \tau \right)\frac{{\omega \tau }}{{1 + \omega ^2 \tau ^2 }}{\text{d}}\left( {\ln \tau } \right)}$$where H(τ) is the distribution function for the relaxation times τ. The methods of the H(τ) evaluation have been elaborated and described in many monographs.