Abstract:Abstract Exposure of concrete to high temperatures affects its mechanical properties by reducing the compressive strength, bending... etc. Factors reducing these properties have been focused on by several studies over the years, producing conflicting results. This article interested an important factor, that is the type of aggregates. For this, an experimental study on the behavior of concrete based on different types of aggregates: calcareous, siliceous and silico-calcareous subjected to high temperatures. In addition, the particle size distribution of the aggregates was chosen to be almost identical so that the latter does not affect the behavior of the concrete. Aggregates and concrete samples were subjected to a heating/cooling cycle of 300, 600 and 800 °C at a speed of 1 °C/ min. The mechanical and physical properties of concrete before and after exposure to high temperatures were studied. In addition, a microstructural study using a scanning electron microscope and a mercury porosimeter was performed. Thus, a comparative study between various researches on the mechanical properties of concrete exposed to high temperatures containing different types of aggregates was carried out. The compressive strength test results showed that the concrete based on siliceous aggregates (C-S) has better mechanical performance up to 300 ° C. However, above 300°C, the compressive strength decreases faster compared to calcareous-based concrete (C-C). According to the mercury porosimeter test, at 600 ° C, C-SC and C-S concretes have the highest number of pores compared to C-C concretes. The microstructure of concrete at high temperatures was influenced mainly by the aggregate’s types and the paste-aggregate transition zone. This study reinforces the importance of standardizing test procedures related to the properties of concrete in a fire situation so that all the results obtained are reproducible and applicable in other research.

Influence of chemical and mineralogical composition of concrete aggregates on their behaviour at elevated temperature

Aggregate Type Influence on Microstructural Behavior of Concrete Exposed to Elevated Temperature

Influence of Elevated Temperatures on the Compressive Strength of Concrete Made with Different Types of Aggregate

Effect of micro‐structural changes on concrete properties at elevated temperature: Current knowledge and outlook

Experimental study on dynamic behavior of concrete at elevated temperatures

Performance of Different Concrete Types Exposed to Elevated Temperatures: A Review

Performance Degradation and Microscopic Analysis of Lightweight Aggregate Concrete after Exposure to High Temperature

Compressive Properties and Microstructure of Modified Lightweight Aggregate Concrete after Exposure to Elevated Temperatures

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

A review of high temperature properties of cement based composites: Effects of nano materials

Mechanical properties of concrete at high temperature—A review

Residual mechanical properties of recycled aggregate concrete at elevated temperatures

Behaviour of Modified Lightweight Aggregate Concrete after Exposure to Elevated Temperatures

Microstructural study of concrete performance after exposure to elevated temperatures via considering C–S–H nanostructure changes

Thermal Resistance, Water Absorption and Microstructure of High-Strength Self-Compacting Lightweight Aggregate Concrete (HSSC-LWAC) after Exposure to Elevated Temperatures

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

Dynamic Tensile Properties and Energy Dissipation of High-Strength Concrete after Exposure to Elevated Temperatures

Performance of Modified Lightweight Aggregate Concrete after Exposure to High Temperatures

Effects of Elevated Temperature on the Residual Behavior of Concrete Containing Marble Dust and Foundry Sand

Microstructure and Mechanical Properties of High-Toughness Fiber-Reinforced Cementitious Composites after Exposure to Elevated Temperatures

Effect of Temperature on Thermal Properties of High-Strength Concrete