Optical, Thermal, and Mechanical Properties of (Y1-xScx)2O3 Transparent Ceramics

Jiquan Huang,Changliang YANG,Qiufeng HUANG,Zhonghua DENG,Yun WANG,Xiaoyun Li,Zehua Zhou,Jian CHEN,Zhuguang LIU,Wang GUO

DOI: https://doi.org/10.21203/rs.3.rs-1113962/v1

2021-11-29

Abstract:Abstract Sesquioxides such as Y 2 O 3 and Sc 2 O 3 are important optical materials, but the fabrication of their transparent ceramics remains a challenge due to the ultra-high melting point of over 2400 o C. In this work, a series of (Y 1- x Sc x ) 2 O 3 transparent ceramics were successfully fabricated by a simple vacuum sintering process without any sintering additives, and the effect of Scandium (Sc) content on the crystal structure and optical/thermal/mechanical properties were evaluated. Y 2 O 3 and Sc 2 O 3 form a complete solid solution with a cubic bixbyite structure. The formation of (Y 1- x Sc x ) 2 O 3 solid solution promotes the densification of ceramics, leading to the realization of high transparency close to the theoretical transmittance over a wide wavelength range of 0.35-8 mm. In particular, the in-line transmittance in the range of 0.6-6 mm remains above 80% for (Y 1- x Sc x ) 2 O 3 with x = 0.23-0.31, while the pristine Y 2 O 3 and Sc 2 O 3 are opaque. Moreover, the mechanical properties including Vickers hardness ( H v ), fracture toughness ( K IC ), and biaxial strength ( δ b ) are evidently enhanced due to the solid solution strengthening, while the thermal conductivity is reduced due to the reduction of photon free path. This study demonstrates that forming of solid solution is a facile and universal approach for preparing sesquioxides transparent ceramics with high optical and mechanical quality.