Fracture Healing and Non-Union

Satoshi Mori

DOI: https://doi.org/10.1007/978-981-16-5613-2_15

2021-12-01

Abstract:Fracture results in loss of its mechanical stability, discontinuity of the bone tissue, and partial destruction of its blood supply. Fracture occurs when mechanical stress over bone integrity is loaded to the bone under the various conditions determined by multiple factors such as magnitude, number, or types of mechanical load and strength of the bone. High energy fracture occurs when a single load higher than the ultimate load is applied to the bone, while fragility fracture occurs when less traumatic load hits fragile bone where structural deterioration by bone loss or degraded bone quality causes reduction of bone mechanical integrity (Fig. 1). Fatigue fracture occurs when repetitive cycles of loading less than the ultimate load are applied to the bone within a certain period. Under repetitive loading conditions, bone as collagen re-enforced calcified material generates microdamage histologically, absorbing loading energy in order to avoid sudden failure, which is named Fatigue in the engineering field. It is considered that microdamage generates even under physiological loadings of daily life such as walking, running, or jumping, then physiologically repaired by normal bone remodeling process [1, 2]. Fatigue fracture occurs as a result of excessive accumulation of microdamage induced by unbalance between microdamage generation and repair. Microdamage generation faster than damage repair causes fatigue fracture. Stress fractures occur under excessive loading conditions in sports or military marching, while atypical femoral fractures (not all) occur under normal loading with over-suppressed bone turnover induced by long-term anti-resorptive use (Fig. 2). The priority of fracture healing is to restore bone connectivity and integrity as soon as possible after fracture. In most fracture healing processes enchondral ossification initially repairs fracture, then completes with the restoration of structure and mechanical integrity of bone to the pre-fractured condition. Fracture healing is complex process that involve the coordination of a sequence of many biological events. The fracture healing process is described as a set of anabolic (bone formation) and catabolic (bone resorption) responses leading to bone healing, delayed, or no union [3]. In addition to the cellular activities, the mechanical factors such as strain, stability act as stimuli for tissue formation during fracture healing, which has not been yet fully understood [4, 5].