Abstract:ABSTRACT Composite membranes were prepared from an aqueous solution of poly(vinyl alcohol) (PVA) and silver sulphate. The silver nanoparticles were generated in situ before crosslinking PVA matrix by reduction of silver ions using sodium borohydride. Physico‐chemical properties of the resulting composite membranes were studied using Fourier transform infrared spectroscopy (FTIR), UV–vis spectroscopy (UV–vis), thermogravimetric analysis (TGA), Wide‐angle X‐ray diffraction (WAXD), scanning electron microscopy (SEM), and universal testing machine (UTM). The UV–vis spectrum shows a single peak at 410 nm due to surface plasmon absorption of silver nanoparticles. This surely specified that silver nanoparticles are generated in PVA matrix. The membranes were under go pervaporation (PV) for separation of water from isopropanol at different temperatures. The results indicated that hydrophilicity and amorphous nature of the membranes were increased with increasing silver nanoparticles in PVA matrix. The swelling and separation performance of the membranes were studied. Both permeation flux and separation factor were increased with increasing silver nanoparticles in PVA matrix. The results showed that the membrane containing 2.5 mass% of Ag salt exhibited excellent PV performance. The values of total flux and flux of water are almost closed to each other, indicating that membranes could be effectively used to break the azeotropic point of water‐isopropanol. The long‐term test was performed at room temperature and ascertained that membranes were durable up to 30 days for the dehydration of IPA. On the basis of the estimate Arrhenius activation energy values, the efficiency of the membranes was discussed. The calculated ΔH s values are negative for all the membranes, indicating that Longmuir's mode of sorption is predominant. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132 , 41248.

Studies on sorption kinetics and sorption isotherm for pervaporative separation of benzene from model pyrolysis gasoline using insitu nano silver/polyvinyl alcohol membrane

Fabrication, characterization and performance analysis of different Ag/PVA nanocomposite membranes for debenzenation of model pyrolysis gasoline using pervaporation

A study on separation of organics by pervaporation

Enhancement of pervaporation performance of composite membranes through in situ generation of silver nanoparticles in poly(vinyl alcohol) matrix

Pervaporation Performance of Polydimethylsiloxane/polyetherimide Composite Membrane for Gasoline Desulphurization(v) Mass Transfer Process Study

Pervaporation Separation of Alkane/Thiophene Mixtures with Pdms Membrane

Separation of Sulfur/Gasoline Mixture with Polydimethylsiloxane/ Polyetherimide Composite Membranes by Pervaporation

Preparation and Pervaporation of A Palygorskite/Polyacrylamide Inorganic-Organic Hybrid Membrane for Separating M-/P-Xylene Isomers

Pervaporation performance of polydimethylsiloxane/polyetherimide composite membrane for gasoline desulphurization (IV) Studies on sulfur specifies

Separation of benzene—n-heptane mixtures by pervaporation with elastomeric membranes. II. Contribution of sorption to the separation mechanism

Pervaporative desulfurization of model gasoline with Ag2O-filled PDMS membranes

Sulfur removal from mixture of n-heptane/organosulfure compound via pervaporation

Recovery Of Petroleum Ether From Solanesol Extracting Solution Through Vacuum Hydrophilic Membrane Distillation

Efficient desulfurization by polymer-inorganic nanocomposite membranes fabricated in reverse microemulsion

Pervaporation separation of<i>n</i>-heptane/organosulfur mixtures with PDMS membrane: Experimental and modelling

Pervaporation Performance of Polydimethylsiloxane Membranes for Separation of Benzene/cyclohexane Mixtures

Pervaporation separation of n-heptane/sulfur species mixtures with polydimethylsiloxane membranes

Sulfur Removal from Gasoline by Pervaporation: the Effect of Hydrocarbon Species

Absorption and desorption of gaseous toluene by an absorbent microcapsules column.

Gas separation of pyrolyzed polymeric membranes: Effect of polymer precursor and pyrolysis conditions

SEPARATION OF PROPANE FROM PROPANE/NITROGEN MIXTURES USING PDMS COMPOSITE MEMBRANES BY VAPOR PERMEATION